Carbon monoxide adsorption on ultra-thin Fe film deposited on Cu(100)

T. Tanabe, Y. Suzuki, T. Wadayama, A. Hatta

Research output: Contribution to journalConference article

20 Citations (Scopus)

Abstract

This paper is mainly concerned with vibrational properties of CO adsorbed on fcc Fe(100) observed using IR reflection absorption spectroscopy. An epitaxial Fe film of eight monolayers has been grown at 300 K on Cu(100). At 0.1 L exposure only a single C-O stretch band appears at 1920 cm-1 which shifts to 1977 cm-1 at 0.55 L. This band further shifts to 1998 cm-1 and saturates in intensity at 0.88 L. In contrast, at 0.25 L a second C-O stretch band appears at 2020 cm-1 which increases in intensity and shifts to 2048 cm-1 at 1.2 L. The initially observed band can be ascribed to the bridging CO and the second band to the on-top CO. Although the bridging CO was stable up to ca. 380 K, the band due to the on-top CO was less stable and disappeared above 313 K. The observed CO adsorption/desorption behavior on the epitaxial fcc Fe(100) surface is compared with that on a vacuum-evaporated bcc Fe polycrystalline film.

Original languageEnglish
Pages (from-to)414-418
Number of pages5
JournalSurface Science
Volume427-428
DOIs
Publication statusPublished - 1999 Jun 1
Externally publishedYes
EventProceedings of the 1998 9th International Conference on Vibrations at Surfaces (VAS9) - Kanagawa-ken, Jpn
Duration: 1998 Oct 121998 Oct 16

ASJC Scopus subject areas

  • Condensed Matter Physics
  • Surfaces and Interfaces
  • Surfaces, Coatings and Films
  • Materials Chemistry

Fingerprint Dive into the research topics of 'Carbon monoxide adsorption on ultra-thin Fe film deposited on Cu(100)'. Together they form a unique fingerprint.

  • Cite this