Cracking and chemical composition of cement paste subjected to heating and water re-curing

Michael Henry, Katsufumi Hashimoto, Ivan Sandi Darma, Takafumi Sugiyama

Research output: Contribution to journalArticle

7 Citations (Scopus)

Abstract

Water re-curing of fire-damaged concrete may reduce the environmental and economic impacts of repair operations by re-using the existing concrete. To clarify the rehydration mechanism, the effects of water re-curing on the microstructure and chemical properties of fire-damaged cement paste were examined. Analysis by X-ray CT showed that heating led to radial cracks that propagated horizontally and vertically in the cement paste specimen. Water supply led to a growth in the cracked space through an increase in the connectivity of the crack network. This growth may be due to expansion caused by the rehydration of CaO into Ca(OH)2. Chemical analyses suggest that the rehydration reaction differs from the initial hydration in that C2S plays a greater role in generating C-S-H gel during the earlier period of water re-curing.

Original languageEnglish
Pages (from-to)134-143
Number of pages10
JournalJournal of Advanced Concrete Technology
Volume14
Issue number4
DOIs
Publication statusPublished - 2016
Externally publishedYes

ASJC Scopus subject areas

  • Building and Construction
  • Materials Science(all)

Fingerprint Dive into the research topics of 'Cracking and chemical composition of cement paste subjected to heating and water re-curing'. Together they form a unique fingerprint.

  • Cite this