Effects of tool rotating rate and pass number on pore structure of A6061 porous aluminum fabricated by using friction stir processing

Takao Utsunomiya, Ken Ichi Tamura, Yoshihiko Hangai, Osamu Kuwazuru, Nobuhiro Yoshikawa

Research output: Contribution to journalArticle

10 Citations (Scopus)

Abstract

As a new fabrication method of porous aluminum with the advantages of high productivity and low manufacturing cost, the authors proposed a fabrication method called the "FSP route precursor method". FSP (friction stir processing) is a solid-state process involving the generation of friction heat and intense plastic flow simply by inserting a rotating tool and allowing it to traverse through the aluminum alloy matrix. In this method, the precursor is manufactured by mixing a blowing agent powder and a stabilization agent powder into the aluminum alloy matrix using the intense stirring action of FSP. Then, porous aluminum can be obtained by foaming the precursor under suitable conditions. In this study, aluminum alloy 6061 (A6061) plates are used as a starting material and porous aluminum is fabricated by applying the procedure of multipass FSP. The effects of the tool rotating rate and the number of passes on the porosity and pore structure of A6061 porous aluminum are investigated. To obtain porous aluminum with high porosity and high quality (i.e., a uniform pore size distribution and highly spherical pores), the tool rotating rate should be approximately from 1000 to 2200 rpm when the rotating tool traverses the matrix four times and the foaming conditions (holding temperature and holding time when the blowing agent is foamed) are optimized. The porous aluminum obtained has a porosity of 70%, and the average equivalent diameter of pores is approximately from 1.5 to 2 mm.

Original languageEnglish
Pages (from-to)542-547
Number of pages6
JournalMaterials Transactions
Volume51
Issue number3
DOIs
Publication statusPublished - 2010 Mar

Fingerprint

Pore structure
Aluminum
friction
Friction
aluminum
porosity
Processing
Aluminum alloys
Blowing agents
aluminum alloys
Porosity
foaming
blowing
Powders
matrices
Fabrication
fabrication
Plastic flow
plastic flow
stirring

Keywords

  • A6061
  • Foam
  • Friction stir processing
  • Pore structure
  • Porosity
  • Porous metals

ASJC Scopus subject areas

  • Materials Science(all)
  • Condensed Matter Physics
  • Mechanical Engineering
  • Mechanics of Materials

Cite this

Effects of tool rotating rate and pass number on pore structure of A6061 porous aluminum fabricated by using friction stir processing. / Utsunomiya, Takao; Tamura, Ken Ichi; Hangai, Yoshihiko; Kuwazuru, Osamu; Yoshikawa, Nobuhiro.

In: Materials Transactions, Vol. 51, No. 3, 03.2010, p. 542-547.

Research output: Contribution to journalArticle

Utsunomiya, Takao ; Tamura, Ken Ichi ; Hangai, Yoshihiko ; Kuwazuru, Osamu ; Yoshikawa, Nobuhiro. / Effects of tool rotating rate and pass number on pore structure of A6061 porous aluminum fabricated by using friction stir processing. In: Materials Transactions. 2010 ; Vol. 51, No. 3. pp. 542-547.
@article{1db1a3e52bd244c98f1a43498bfa8483,
title = "Effects of tool rotating rate and pass number on pore structure of A6061 porous aluminum fabricated by using friction stir processing",
abstract = "As a new fabrication method of porous aluminum with the advantages of high productivity and low manufacturing cost, the authors proposed a fabrication method called the {"}FSP route precursor method{"}. FSP (friction stir processing) is a solid-state process involving the generation of friction heat and intense plastic flow simply by inserting a rotating tool and allowing it to traverse through the aluminum alloy matrix. In this method, the precursor is manufactured by mixing a blowing agent powder and a stabilization agent powder into the aluminum alloy matrix using the intense stirring action of FSP. Then, porous aluminum can be obtained by foaming the precursor under suitable conditions. In this study, aluminum alloy 6061 (A6061) plates are used as a starting material and porous aluminum is fabricated by applying the procedure of multipass FSP. The effects of the tool rotating rate and the number of passes on the porosity and pore structure of A6061 porous aluminum are investigated. To obtain porous aluminum with high porosity and high quality (i.e., a uniform pore size distribution and highly spherical pores), the tool rotating rate should be approximately from 1000 to 2200 rpm when the rotating tool traverses the matrix four times and the foaming conditions (holding temperature and holding time when the blowing agent is foamed) are optimized. The porous aluminum obtained has a porosity of 70{\%}, and the average equivalent diameter of pores is approximately from 1.5 to 2 mm.",
keywords = "A6061, Foam, Friction stir processing, Pore structure, Porosity, Porous metals",
author = "Takao Utsunomiya and Tamura, {Ken Ichi} and Yoshihiko Hangai and Osamu Kuwazuru and Nobuhiro Yoshikawa",
year = "2010",
month = "3",
doi = "10.2320/matertrans.MBW200916",
language = "English",
volume = "51",
pages = "542--547",
journal = "Materials Transactions",
issn = "1345-9678",
publisher = "Japan Institute of Metals (JIM)",
number = "3",

}

TY - JOUR

T1 - Effects of tool rotating rate and pass number on pore structure of A6061 porous aluminum fabricated by using friction stir processing

AU - Utsunomiya, Takao

AU - Tamura, Ken Ichi

AU - Hangai, Yoshihiko

AU - Kuwazuru, Osamu

AU - Yoshikawa, Nobuhiro

PY - 2010/3

Y1 - 2010/3

N2 - As a new fabrication method of porous aluminum with the advantages of high productivity and low manufacturing cost, the authors proposed a fabrication method called the "FSP route precursor method". FSP (friction stir processing) is a solid-state process involving the generation of friction heat and intense plastic flow simply by inserting a rotating tool and allowing it to traverse through the aluminum alloy matrix. In this method, the precursor is manufactured by mixing a blowing agent powder and a stabilization agent powder into the aluminum alloy matrix using the intense stirring action of FSP. Then, porous aluminum can be obtained by foaming the precursor under suitable conditions. In this study, aluminum alloy 6061 (A6061) plates are used as a starting material and porous aluminum is fabricated by applying the procedure of multipass FSP. The effects of the tool rotating rate and the number of passes on the porosity and pore structure of A6061 porous aluminum are investigated. To obtain porous aluminum with high porosity and high quality (i.e., a uniform pore size distribution and highly spherical pores), the tool rotating rate should be approximately from 1000 to 2200 rpm when the rotating tool traverses the matrix four times and the foaming conditions (holding temperature and holding time when the blowing agent is foamed) are optimized. The porous aluminum obtained has a porosity of 70%, and the average equivalent diameter of pores is approximately from 1.5 to 2 mm.

AB - As a new fabrication method of porous aluminum with the advantages of high productivity and low manufacturing cost, the authors proposed a fabrication method called the "FSP route precursor method". FSP (friction stir processing) is a solid-state process involving the generation of friction heat and intense plastic flow simply by inserting a rotating tool and allowing it to traverse through the aluminum alloy matrix. In this method, the precursor is manufactured by mixing a blowing agent powder and a stabilization agent powder into the aluminum alloy matrix using the intense stirring action of FSP. Then, porous aluminum can be obtained by foaming the precursor under suitable conditions. In this study, aluminum alloy 6061 (A6061) plates are used as a starting material and porous aluminum is fabricated by applying the procedure of multipass FSP. The effects of the tool rotating rate and the number of passes on the porosity and pore structure of A6061 porous aluminum are investigated. To obtain porous aluminum with high porosity and high quality (i.e., a uniform pore size distribution and highly spherical pores), the tool rotating rate should be approximately from 1000 to 2200 rpm when the rotating tool traverses the matrix four times and the foaming conditions (holding temperature and holding time when the blowing agent is foamed) are optimized. The porous aluminum obtained has a porosity of 70%, and the average equivalent diameter of pores is approximately from 1.5 to 2 mm.

KW - A6061

KW - Foam

KW - Friction stir processing

KW - Pore structure

KW - Porosity

KW - Porous metals

UR - http://www.scopus.com/inward/record.url?scp=77951582976&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=77951582976&partnerID=8YFLogxK

U2 - 10.2320/matertrans.MBW200916

DO - 10.2320/matertrans.MBW200916

M3 - Article

VL - 51

SP - 542

EP - 547

JO - Materials Transactions

JF - Materials Transactions

SN - 1345-9678

IS - 3

ER -