Formation of corrosion-resistant films on AlZnMg alloy by steam coating using acidic Zn(NO3)2 aqueous solutions+

Tetsuya Yokomizo, Yuta Shimada, Mika Tsunakawa, Ai Serizawa, Takahiro Ishizaki

Research output: Contribution to journalArticle

Abstract

Corrosion-resistant films were fabricated on AlZnMg alloy by steam coating using an acidic aqueous solution of Zn(NO3)2 at different concentrations. X-ray diffraction patterns and Fourier transform-infrared spectrometer spectra demonstrated that nitrate-type ZnAl layered double hydroxide (LDH) and ZnO films were formed on the AlZnMg surface by steam coating at temperatures of 373, 433, and 473 K, using Zn(NO3)2 aqueous solution at 1000 mM. At 513 K, £-AlO(OH) films were formed on the AlZnMg surface by steam coating using 1 to 100 mM Zn(NO3)2 aqueous solution. The corrosion resistance of the films was investigated by potentiodynamic polarization curve measurements, which revealed that the £-AlO(OH) films prepared by steam coating at 513 K using 1 mM of Zn(NO3)2 aqueous solution was the most effective treatment for suppression of pitting corrosion and anodic current density.

Original languageEnglish
Pages (from-to)1166-1172
Number of pages7
JournalMaterials Transactions
Volume59
Issue number7
DOIs
Publication statusPublished - 2018 Jan 1

Keywords

  • AlZnMg alloy
  • Corrosion resistance
  • Layered double hydroxide
  • Steam coating process

ASJC Scopus subject areas

  • Materials Science(all)
  • Condensed Matter Physics
  • Mechanics of Materials
  • Mechanical Engineering

Fingerprint Dive into the research topics of 'Formation of corrosion-resistant films on AlZnMg alloy by steam coating using acidic Zn(NO<sub>3</sub>)<sub>2</sub> aqueous solutions<sup>+</sup>'. Together they form a unique fingerprint.

  • Cite this