Fracture toughness of SmBaCuO bulk superconductors at cryogenic temperatures

Yasuhiro Yoshino, Akira Iwabuchi, Naoki Takahashi, Kazumune Katagiri, Koshichi Noto, Naomichi Sakai, Masato Murakami

Research output: Contribution to journalArticle

6 Citations (Scopus)

Abstract

Fracture toughness of Sm123 bulk superconductors with 16.7 and 28.6 mol% of Sm211 particles have been investigated by Vickers hardness test at cryogenic temperatures. The hardness test was carried out on (001) plane for two types of SmBCO bulk materials during 40-293 K. The hardness of Sm17 became constant to 5,000 MPa during 40-293 K. However, the hardness of Sm29 increased to 7,380 MPa with decreasing temperatures. In addition, fracture toughness of Sm17 and Sm29 will be discussed calculating from Vickers hardness, Median crack length, Young's modulus and applied load. The fracture toughness of Sm17 became constant to 0.8 MPa√m following the hardness property. The fracture toughness of Sm29 decreased from 0.73 MPa√m at 293 K to 0.67 MPa√m at 40 K.

Original languageEnglish
Pages (from-to)1118-1121
Number of pages4
JournalIEEE Transactions on Applied Superconductivity
Volume14
Issue number2
DOIs
Publication statusPublished - 2004 Jun

Fingerprint

cryogenic temperature
fracture strength
Cryogenics
Superconducting materials
Fracture toughness
Hardness
hardness tests
hardness
Vickers hardness
Temperature
Loads (forces)
modulus of elasticity
cracks
Elastic moduli
Cracks
temperature

Keywords

  • Cryogenic temperatures
  • Deformation mechanism
  • Fracture toughness
  • Vickers hardness

ASJC Scopus subject areas

  • Electrical and Electronic Engineering
  • Physics and Astronomy (miscellaneous)

Cite this

Fracture toughness of SmBaCuO bulk superconductors at cryogenic temperatures. / Yoshino, Yasuhiro; Iwabuchi, Akira; Takahashi, Naoki; Katagiri, Kazumune; Noto, Koshichi; Sakai, Naomichi; Murakami, Masato.

In: IEEE Transactions on Applied Superconductivity, Vol. 14, No. 2, 06.2004, p. 1118-1121.

Research output: Contribution to journalArticle

Yoshino, Yasuhiro ; Iwabuchi, Akira ; Takahashi, Naoki ; Katagiri, Kazumune ; Noto, Koshichi ; Sakai, Naomichi ; Murakami, Masato. / Fracture toughness of SmBaCuO bulk superconductors at cryogenic temperatures. In: IEEE Transactions on Applied Superconductivity. 2004 ; Vol. 14, No. 2. pp. 1118-1121.
@article{5da5d6aa088644b4b83119cbf6b08bbb,
title = "Fracture toughness of SmBaCuO bulk superconductors at cryogenic temperatures",
abstract = "Fracture toughness of Sm123 bulk superconductors with 16.7 and 28.6 mol{\%} of Sm211 particles have been investigated by Vickers hardness test at cryogenic temperatures. The hardness test was carried out on (001) plane for two types of SmBCO bulk materials during 40-293 K. The hardness of Sm17 became constant to 5,000 MPa during 40-293 K. However, the hardness of Sm29 increased to 7,380 MPa with decreasing temperatures. In addition, fracture toughness of Sm17 and Sm29 will be discussed calculating from Vickers hardness, Median crack length, Young's modulus and applied load. The fracture toughness of Sm17 became constant to 0.8 MPa√m following the hardness property. The fracture toughness of Sm29 decreased from 0.73 MPa√m at 293 K to 0.67 MPa√m at 40 K.",
keywords = "Cryogenic temperatures, Deformation mechanism, Fracture toughness, Vickers hardness",
author = "Yasuhiro Yoshino and Akira Iwabuchi and Naoki Takahashi and Kazumune Katagiri and Koshichi Noto and Naomichi Sakai and Masato Murakami",
year = "2004",
month = "6",
doi = "10.1109/TASC.2004.830438",
language = "English",
volume = "14",
pages = "1118--1121",
journal = "IEEE Transactions on Applied Superconductivity",
issn = "1051-8223",
publisher = "Institute of Electrical and Electronics Engineers Inc.",
number = "2",

}

TY - JOUR

T1 - Fracture toughness of SmBaCuO bulk superconductors at cryogenic temperatures

AU - Yoshino, Yasuhiro

AU - Iwabuchi, Akira

AU - Takahashi, Naoki

AU - Katagiri, Kazumune

AU - Noto, Koshichi

AU - Sakai, Naomichi

AU - Murakami, Masato

PY - 2004/6

Y1 - 2004/6

N2 - Fracture toughness of Sm123 bulk superconductors with 16.7 and 28.6 mol% of Sm211 particles have been investigated by Vickers hardness test at cryogenic temperatures. The hardness test was carried out on (001) plane for two types of SmBCO bulk materials during 40-293 K. The hardness of Sm17 became constant to 5,000 MPa during 40-293 K. However, the hardness of Sm29 increased to 7,380 MPa with decreasing temperatures. In addition, fracture toughness of Sm17 and Sm29 will be discussed calculating from Vickers hardness, Median crack length, Young's modulus and applied load. The fracture toughness of Sm17 became constant to 0.8 MPa√m following the hardness property. The fracture toughness of Sm29 decreased from 0.73 MPa√m at 293 K to 0.67 MPa√m at 40 K.

AB - Fracture toughness of Sm123 bulk superconductors with 16.7 and 28.6 mol% of Sm211 particles have been investigated by Vickers hardness test at cryogenic temperatures. The hardness test was carried out on (001) plane for two types of SmBCO bulk materials during 40-293 K. The hardness of Sm17 became constant to 5,000 MPa during 40-293 K. However, the hardness of Sm29 increased to 7,380 MPa with decreasing temperatures. In addition, fracture toughness of Sm17 and Sm29 will be discussed calculating from Vickers hardness, Median crack length, Young's modulus and applied load. The fracture toughness of Sm17 became constant to 0.8 MPa√m following the hardness property. The fracture toughness of Sm29 decreased from 0.73 MPa√m at 293 K to 0.67 MPa√m at 40 K.

KW - Cryogenic temperatures

KW - Deformation mechanism

KW - Fracture toughness

KW - Vickers hardness

UR - http://www.scopus.com/inward/record.url?scp=4344569488&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=4344569488&partnerID=8YFLogxK

U2 - 10.1109/TASC.2004.830438

DO - 10.1109/TASC.2004.830438

M3 - Article

VL - 14

SP - 1118

EP - 1121

JO - IEEE Transactions on Applied Superconductivity

JF - IEEE Transactions on Applied Superconductivity

SN - 1051-8223

IS - 2

ER -