Friction and wear properties of CrAlN and CrVN films deposited by cathodic arc ion plating method

M. Uchida, N. Nihira, A. Mitsuo, K. Toyoda, K. Kubota, T. Aizawa

Research output: Contribution to journalArticle

177 Citations (Scopus)

Abstract

Chromium nitride (CrN) films are superior to the titanium nitride film in corrosion and wear resistances, and friction behavior. CrN has been widely applied to the molding dies, machine parts and sliding part. In the present paper, additions of aluminum and vanadium into CrN films were performed with an expectation of improvement in tribological properties. CrN, CrAlN and CrVN were deposited by a cathodic arc ion plating. Deposited films were characterized by X-ray diffraction for crystal structure identification and energy-dispersive X-ray spectroscopy for chemical composition analysis. Diffraction peaks that appeared were similar in position and orientation in all films because the crystal structure and the lattice constant for CrN, VN and AlN are close to each other. The composition of the film deposited with Al and V was estimated to be Cr70Al30N and Cr50V50N, respectively. Knoop hardness test showed that CrAlN was harder than CrN and CrVN. Friction and wear tests were carried out by a ball-on-disk tribometer with stainless steel and cemented carbide balls as a counter material, with and without lubricant. Flaking occurred on CrN with stainless steel ball in wear tests without lubrication by ball-on-disk tribometer, but that did not occur on CrAlN and CrVN films. In the case of the wear test with cemented carbide ball, depth of wear track on CrN film reached to the substrate. The friction coefficient was almost the same for CrN and CrAlN films; however, that for CrVN film was lower than other films, in motor oil. V addition into CrN film successfully improved its tribological properties.

Original languageEnglish
Pages (from-to)627-630
Number of pages4
JournalSurface and Coatings Technology
Volume177-178
DOIs
Publication statusPublished - 2004 Jan 30
Externally publishedYes

Fingerprint

ion plating
Plating
Chromium
Nitrides
friction
arcs
nitrides
Wear of materials
chromium
Ions
Friction
balls
wear tests
tribometers
Stainless Steel
carbides
Carbides
stainless steels
Stainless steel
Crystal structure

Keywords

  • Cathodic arc ion plating
  • Chromium aluminum nitride
  • Chromium nitride
  • Chromium vanadium nitride
  • Friction coefficient
  • Wear

ASJC Scopus subject areas

  • Surfaces, Coatings and Films
  • Condensed Matter Physics
  • Surfaces and Interfaces

Cite this

Friction and wear properties of CrAlN and CrVN films deposited by cathodic arc ion plating method. / Uchida, M.; Nihira, N.; Mitsuo, A.; Toyoda, K.; Kubota, K.; Aizawa, T.

In: Surface and Coatings Technology, Vol. 177-178, 30.01.2004, p. 627-630.

Research output: Contribution to journalArticle

Uchida, M. ; Nihira, N. ; Mitsuo, A. ; Toyoda, K. ; Kubota, K. ; Aizawa, T. / Friction and wear properties of CrAlN and CrVN films deposited by cathodic arc ion plating method. In: Surface and Coatings Technology. 2004 ; Vol. 177-178. pp. 627-630.
@article{f74b06b510f648eeb568685f7a20bef7,
title = "Friction and wear properties of CrAlN and CrVN films deposited by cathodic arc ion plating method",
abstract = "Chromium nitride (CrN) films are superior to the titanium nitride film in corrosion and wear resistances, and friction behavior. CrN has been widely applied to the molding dies, machine parts and sliding part. In the present paper, additions of aluminum and vanadium into CrN films were performed with an expectation of improvement in tribological properties. CrN, CrAlN and CrVN were deposited by a cathodic arc ion plating. Deposited films were characterized by X-ray diffraction for crystal structure identification and energy-dispersive X-ray spectroscopy for chemical composition analysis. Diffraction peaks that appeared were similar in position and orientation in all films because the crystal structure and the lattice constant for CrN, VN and AlN are close to each other. The composition of the film deposited with Al and V was estimated to be Cr70Al30N and Cr50V50N, respectively. Knoop hardness test showed that CrAlN was harder than CrN and CrVN. Friction and wear tests were carried out by a ball-on-disk tribometer with stainless steel and cemented carbide balls as a counter material, with and without lubricant. Flaking occurred on CrN with stainless steel ball in wear tests without lubrication by ball-on-disk tribometer, but that did not occur on CrAlN and CrVN films. In the case of the wear test with cemented carbide ball, depth of wear track on CrN film reached to the substrate. The friction coefficient was almost the same for CrN and CrAlN films; however, that for CrVN film was lower than other films, in motor oil. V addition into CrN film successfully improved its tribological properties.",
keywords = "Cathodic arc ion plating, Chromium aluminum nitride, Chromium nitride, Chromium vanadium nitride, Friction coefficient, Wear",
author = "M. Uchida and N. Nihira and A. Mitsuo and K. Toyoda and K. Kubota and T. Aizawa",
year = "2004",
month = "1",
day = "30",
doi = "10.1016/S0257-8972(03)00937-X",
language = "English",
volume = "177-178",
pages = "627--630",
journal = "Surface and Coatings Technology",
issn = "0257-8972",
publisher = "Elsevier",

}

TY - JOUR

T1 - Friction and wear properties of CrAlN and CrVN films deposited by cathodic arc ion plating method

AU - Uchida, M.

AU - Nihira, N.

AU - Mitsuo, A.

AU - Toyoda, K.

AU - Kubota, K.

AU - Aizawa, T.

PY - 2004/1/30

Y1 - 2004/1/30

N2 - Chromium nitride (CrN) films are superior to the titanium nitride film in corrosion and wear resistances, and friction behavior. CrN has been widely applied to the molding dies, machine parts and sliding part. In the present paper, additions of aluminum and vanadium into CrN films were performed with an expectation of improvement in tribological properties. CrN, CrAlN and CrVN were deposited by a cathodic arc ion plating. Deposited films were characterized by X-ray diffraction for crystal structure identification and energy-dispersive X-ray spectroscopy for chemical composition analysis. Diffraction peaks that appeared were similar in position and orientation in all films because the crystal structure and the lattice constant for CrN, VN and AlN are close to each other. The composition of the film deposited with Al and V was estimated to be Cr70Al30N and Cr50V50N, respectively. Knoop hardness test showed that CrAlN was harder than CrN and CrVN. Friction and wear tests were carried out by a ball-on-disk tribometer with stainless steel and cemented carbide balls as a counter material, with and without lubricant. Flaking occurred on CrN with stainless steel ball in wear tests without lubrication by ball-on-disk tribometer, but that did not occur on CrAlN and CrVN films. In the case of the wear test with cemented carbide ball, depth of wear track on CrN film reached to the substrate. The friction coefficient was almost the same for CrN and CrAlN films; however, that for CrVN film was lower than other films, in motor oil. V addition into CrN film successfully improved its tribological properties.

AB - Chromium nitride (CrN) films are superior to the titanium nitride film in corrosion and wear resistances, and friction behavior. CrN has been widely applied to the molding dies, machine parts and sliding part. In the present paper, additions of aluminum and vanadium into CrN films were performed with an expectation of improvement in tribological properties. CrN, CrAlN and CrVN were deposited by a cathodic arc ion plating. Deposited films were characterized by X-ray diffraction for crystal structure identification and energy-dispersive X-ray spectroscopy for chemical composition analysis. Diffraction peaks that appeared were similar in position and orientation in all films because the crystal structure and the lattice constant for CrN, VN and AlN are close to each other. The composition of the film deposited with Al and V was estimated to be Cr70Al30N and Cr50V50N, respectively. Knoop hardness test showed that CrAlN was harder than CrN and CrVN. Friction and wear tests were carried out by a ball-on-disk tribometer with stainless steel and cemented carbide balls as a counter material, with and without lubricant. Flaking occurred on CrN with stainless steel ball in wear tests without lubrication by ball-on-disk tribometer, but that did not occur on CrAlN and CrVN films. In the case of the wear test with cemented carbide ball, depth of wear track on CrN film reached to the substrate. The friction coefficient was almost the same for CrN and CrAlN films; however, that for CrVN film was lower than other films, in motor oil. V addition into CrN film successfully improved its tribological properties.

KW - Cathodic arc ion plating

KW - Chromium aluminum nitride

KW - Chromium nitride

KW - Chromium vanadium nitride

KW - Friction coefficient

KW - Wear

UR - http://www.scopus.com/inward/record.url?scp=1342290023&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=1342290023&partnerID=8YFLogxK

U2 - 10.1016/S0257-8972(03)00937-X

DO - 10.1016/S0257-8972(03)00937-X

M3 - Article

VL - 177-178

SP - 627

EP - 630

JO - Surface and Coatings Technology

JF - Surface and Coatings Technology

SN - 0257-8972

ER -