Improvement in the Performance of Bulk MgB2 Material through Optimization of Sintering Process

Research output: Chapter in Book/Report/Conference proceedingConference contribution

2 Citations (Scopus)

Abstract

Enhancement of the critical current density (Jc) in MgB2 bulk material is very important for engineering applications. It has been found that the optimization of the sintering temperature leads to high Jc values in bulk MgB2 material. In our recent work, the highest trapped field value was recorded in the sample sintered at 775oC. The present investigation has focused on methods to improve further Jc values of the disk-shape bulk MgB2 superconductors by optimizing sintering conditions. MgB2 samples were subjected to a solid state reaction at 775, 780, 785, 795, 800 and 805oC for 3 h in pure Ar atmosphere. XRD analysis showed that all the samples were single phase MgB2. The magnetization measurements confirmed a sharp superconducting transition with onset Tc at around 38.7 K. Atomic force microscopy observation indicated that the number of nano meter size grains is more in samples processed 3 h at 805oC has compared to the samples sintered at 775oC. As a result, the highest Jc value of 245 kA/cm2 at 20 K was obtained for the sample sintered at 805oC for 3 h.

Original languageEnglish
Title of host publicationPhysics Procedia
PublisherElsevier
Pages73-76
Number of pages4
Volume65
DOIs
Publication statusPublished - 2015
Event27th International Symposium on Superconductivity, ISS 2014 - Tokyo, Japan
Duration: 2014 Nov 252014 Nov 27

Other

Other27th International Symposium on Superconductivity, ISS 2014
CountryJapan
CityTokyo
Period14/11/2514/11/27

Fingerprint

sintering
optimization
disks (shapes)
critical current
grain size
atomic force microscopy
engineering
current density
solid state
atmospheres
magnetization
augmentation
temperature

Keywords

  • critical current density
  • magnetization measurements
  • MgB2
  • sintering time
  • X-ray diffraction

ASJC Scopus subject areas

  • Physics and Astronomy(all)

Cite this

Improvement in the Performance of Bulk MgB2 Material through Optimization of Sintering Process. / Kobayashi, H.; Miryala, Muralidhar; Koblischka, Michael Rudolf; Inoue, Kazuo; Murakami, Masato.

Physics Procedia. Vol. 65 Elsevier, 2015. p. 73-76.

Research output: Chapter in Book/Report/Conference proceedingConference contribution

Kobayashi, H, Miryala, M, Koblischka, MR, Inoue, K & Murakami, M 2015, Improvement in the Performance of Bulk MgB2 Material through Optimization of Sintering Process. in Physics Procedia. vol. 65, Elsevier, pp. 73-76, 27th International Symposium on Superconductivity, ISS 2014, Tokyo, Japan, 14/11/25. https://doi.org/10.1016/j.phpro.2015.05.127
@inproceedings{06d6250481e04c86b78ef3d8e5384a7d,
title = "Improvement in the Performance of Bulk MgB2 Material through Optimization of Sintering Process",
abstract = "Enhancement of the critical current density (Jc) in MgB2 bulk material is very important for engineering applications. It has been found that the optimization of the sintering temperature leads to high Jc values in bulk MgB2 material. In our recent work, the highest trapped field value was recorded in the sample sintered at 775oC. The present investigation has focused on methods to improve further Jc values of the disk-shape bulk MgB2 superconductors by optimizing sintering conditions. MgB2 samples were subjected to a solid state reaction at 775, 780, 785, 795, 800 and 805oC for 3 h in pure Ar atmosphere. XRD analysis showed that all the samples were single phase MgB2. The magnetization measurements confirmed a sharp superconducting transition with onset Tc at around 38.7 K. Atomic force microscopy observation indicated that the number of nano meter size grains is more in samples processed 3 h at 805oC has compared to the samples sintered at 775oC. As a result, the highest Jc value of 245 kA/cm2 at 20 K was obtained for the sample sintered at 805oC for 3 h.",
keywords = "critical current density, magnetization measurements, MgB2, sintering time, X-ray diffraction",
author = "H. Kobayashi and Muralidhar Miryala and Koblischka, {Michael Rudolf} and Kazuo Inoue and Masato Murakami",
year = "2015",
doi = "10.1016/j.phpro.2015.05.127",
language = "English",
volume = "65",
pages = "73--76",
booktitle = "Physics Procedia",
publisher = "Elsevier",

}

TY - GEN

T1 - Improvement in the Performance of Bulk MgB2 Material through Optimization of Sintering Process

AU - Kobayashi, H.

AU - Miryala, Muralidhar

AU - Koblischka, Michael Rudolf

AU - Inoue, Kazuo

AU - Murakami, Masato

PY - 2015

Y1 - 2015

N2 - Enhancement of the critical current density (Jc) in MgB2 bulk material is very important for engineering applications. It has been found that the optimization of the sintering temperature leads to high Jc values in bulk MgB2 material. In our recent work, the highest trapped field value was recorded in the sample sintered at 775oC. The present investigation has focused on methods to improve further Jc values of the disk-shape bulk MgB2 superconductors by optimizing sintering conditions. MgB2 samples were subjected to a solid state reaction at 775, 780, 785, 795, 800 and 805oC for 3 h in pure Ar atmosphere. XRD analysis showed that all the samples were single phase MgB2. The magnetization measurements confirmed a sharp superconducting transition with onset Tc at around 38.7 K. Atomic force microscopy observation indicated that the number of nano meter size grains is more in samples processed 3 h at 805oC has compared to the samples sintered at 775oC. As a result, the highest Jc value of 245 kA/cm2 at 20 K was obtained for the sample sintered at 805oC for 3 h.

AB - Enhancement of the critical current density (Jc) in MgB2 bulk material is very important for engineering applications. It has been found that the optimization of the sintering temperature leads to high Jc values in bulk MgB2 material. In our recent work, the highest trapped field value was recorded in the sample sintered at 775oC. The present investigation has focused on methods to improve further Jc values of the disk-shape bulk MgB2 superconductors by optimizing sintering conditions. MgB2 samples were subjected to a solid state reaction at 775, 780, 785, 795, 800 and 805oC for 3 h in pure Ar atmosphere. XRD analysis showed that all the samples were single phase MgB2. The magnetization measurements confirmed a sharp superconducting transition with onset Tc at around 38.7 K. Atomic force microscopy observation indicated that the number of nano meter size grains is more in samples processed 3 h at 805oC has compared to the samples sintered at 775oC. As a result, the highest Jc value of 245 kA/cm2 at 20 K was obtained for the sample sintered at 805oC for 3 h.

KW - critical current density

KW - magnetization measurements

KW - MgB2

KW - sintering time

KW - X-ray diffraction

UR - http://www.scopus.com/inward/record.url?scp=84948418913&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=84948418913&partnerID=8YFLogxK

U2 - 10.1016/j.phpro.2015.05.127

DO - 10.1016/j.phpro.2015.05.127

M3 - Conference contribution

AN - SCOPUS:84948418913

VL - 65

SP - 73

EP - 76

BT - Physics Procedia

PB - Elsevier

ER -