Improvement of critical current density of MgB2 bulk superconductor processed by Spark Plasma Sintering

Jacques G. Noudem, Yiteng Xing, Pierre Bernstein, Richard Retoux, Masaki Higuchi, Srikanth S. Arvapalli, Miryala Muralidhar, Masato Murakami

Research output: Contribution to journalArticle

Abstract

Spark Plasma Sintering (SPS) is a promising rapid consolidation technique that allows a better understanding and optimization of the sintering kinetics and therefore makes it possible to obtain MgB2 bulk superconductor with tailored microstructures consisting of grains with either spherical or elongated morphology. In this contribution, the role of the precursor powders on the superconducting properties of MgB2 is investigated. Three sets of bulk MgB2 material were processed from: (i) a commercially available MgB2 powder; (ii) a mixture of Mg metal and amorphous B using a single-step solid-state reaction process and (iii) a mixture of amorphous boron coated with carbon and Mg metal. The samples were prepared in the same SPS processing conditions. The microstructure of the samples was investigated by X-ray diffraction, SEM and TEM and correlated to their superconducting properties. The critical current density of the best sample at 20K was Jc = 500 kA/cm2 in self-field, which is one of the highest critical current density reported for MgB2 bulk superconductors.

Original languageEnglish
JournalJournal of the American Ceramic Society
DOIs
Publication statusAccepted/In press - 2020

Keywords

  • critical current density (J)
  • flux pinning
  • MgB
  • microstructure
  • spark plasma sintering

ASJC Scopus subject areas

  • Ceramics and Composites
  • Materials Chemistry

Fingerprint Dive into the research topics of 'Improvement of critical current density of MgB<sub>2</sub> bulk superconductor processed by Spark Plasma Sintering'. Together they form a unique fingerprint.

  • Cite this