In-situ powder neutron diffraction study on the formation process of LaMg2NiH7

Toyoto Sato, Kazutaka Ikeda, Motoaki Matsuo, Kazutoshi Miwa, Toshiya Otomo, Stefano Deledda, Bjørn C. Hauback, Guanqiao Li, Shigeyuki Takagi, Shin ichi Orimo

Research output: Contribution to journalArticlepeer-review

9 Citations (Scopus)

Abstract

The formation process from the intermetallic compound LaMg2Ni to a complex hydride (deuteride) LaMg2NiD7 composed of La3+, 2 × Mg2+, [NiD4]4−, and 3 × D was investigated by in-situ powder neutron diffraction under deuterium gas pressure at room temperature. Below 0.001 MPa, small amount of deuterium was initially dissolved in the lattice of LaMg2Ni forming LaMg2NiD0.05 and two new hydride phases (LaMg2NiDx1 and LaMg2NiDx2) were continuously yielded. Furthermore, LaMg2NiD4.6 with NiD1.9 and NiD3.3 units and interstitial deuterium atoms was formed prior to appearing of LaMg2NiD7. From their Bragg peak positions, the deuterium contents x1, and x2 were inferred as 0.05 < x1 < x2 < 4.6. At approximately 0.001 MPa, LaMg2NiD7 started forming. Since the intermediate deuterides had similar metal atomic framework of LaMg2Ni, we revealed that LaMg2NiD7 formation proceeded through multiple deuteride phases with maintaining of the metal atomic framework of LaMg2Ni.

Original languageEnglish
Pages (from-to)22449-22453
Number of pages5
JournalInternational Journal of Hydrogen Energy
Volume42
Issue number35
DOIs
Publication statusPublished - 2017 Aug 31
Externally publishedYes

Keywords

  • Complex hydride
  • Crystal structure
  • In-situ powder neutron diffraction

ASJC Scopus subject areas

  • Renewable Energy, Sustainability and the Environment
  • Fuel Technology
  • Condensed Matter Physics
  • Energy Engineering and Power Technology

Fingerprint

Dive into the research topics of 'In-situ powder neutron diffraction study on the formation process of LaMg<sub>2</sub>NiH<sub>7</sub>'. Together they form a unique fingerprint.

Cite this