Influence of additions and radiation damage on the superconducting properties of sintered YBa2Cu3O7 - gd

Michael Rudolf Koblischka, Th Schuster, H. Kronmüller

Research output: Contribution to journalArticle

16 Citations (Scopus)

Abstract

Using the high-resolution Faraday (HRF) technique, domain patterns of sintered YBa2Cu3O7 - δ samples containing additions of Ag2O and Y2BaCuO5 are obtained. Similar observations are carried out on sintered YBa2Cu3O7-δ samples with reduced oxygen content and on electron-irradiated samples. The penetration of flux into sintered high-Tc superconductors is found to be totally different from single crystalline materials (single crystals and epitaxial thin films) as the Abrikosov vortices penetrate the sample not as a whole thus forming a so-called flux front. Only a flux penetration into single superconducting grains is observed. From the measured flux density profiles, the intragrain critical current densities are determined locally. It is found that the chemical impurity phases do not affect the intragranular flux density distribution and the intragranular critical current density, but the decomposition of the Ag2O leads to an improved oxygen stoichiometry in these samples. Electron irradiation is found to enhance the intragrain critical current densities, whereas the oxygen reduction leads to reduced intragrain currents. To determine the influence of the additions also on the intergrain critical current densities, standard four-point transport current measurements are carried out on the same samples. It is found that a maximum enhancement of the critical current density is obtained by the addition of 10 wt% silver oxide; however, this critical current density is drastically reduced by applying small external magnetic fields. The lower critical field of the matrix and the corresponding Josephson penetration depth are determined from transport current measurements. The Ag2O additions and the green phase particles are found to separate the superconducting YBa2Cu3O7-δ grains. The resulting larger widths of the barriers between the superconducting grains are found to cause a stronger influence of external magnetic fields on the intergrain critical current densities.

Original languageEnglish
Pages (from-to)263-278
Number of pages16
JournalPhysica C: Superconductivity and its Applications
Volume211
Issue number3-4
DOIs
Publication statusPublished - 1993 Jun 20
Externally publishedYes

Fingerprint

Radiation damage
radiation damage
critical current
current density
Fluxes
damage
Electric current measurement
Oxygen
penetration
Silver oxides
Magnetic fields
Electron irradiation
oxygen
Epitaxial films
flux density
Stoichiometry
silver oxides
Superconducting materials
Vortex flow
electron irradiation

ASJC Scopus subject areas

  • Electronic, Optical and Magnetic Materials
  • Condensed Matter Physics
  • Energy Engineering and Power Technology
  • Electrical and Electronic Engineering

Cite this

Influence of additions and radiation damage on the superconducting properties of sintered YBa2Cu3O7 - gd. / Koblischka, Michael Rudolf; Schuster, Th; Kronmüller, H.

In: Physica C: Superconductivity and its Applications, Vol. 211, No. 3-4, 20.06.1993, p. 263-278.

Research output: Contribution to journalArticle

@article{535fa16d3a9246acbba5ed4bf44b67cc,
title = "Influence of additions and radiation damage on the superconducting properties of sintered YBa2Cu3O7 - gd",
abstract = "Using the high-resolution Faraday (HRF) technique, domain patterns of sintered YBa2Cu3O7 - δ samples containing additions of Ag2O and Y2BaCuO5 are obtained. Similar observations are carried out on sintered YBa2Cu3O7-δ samples with reduced oxygen content and on electron-irradiated samples. The penetration of flux into sintered high-Tc superconductors is found to be totally different from single crystalline materials (single crystals and epitaxial thin films) as the Abrikosov vortices penetrate the sample not as a whole thus forming a so-called flux front. Only a flux penetration into single superconducting grains is observed. From the measured flux density profiles, the intragrain critical current densities are determined locally. It is found that the chemical impurity phases do not affect the intragranular flux density distribution and the intragranular critical current density, but the decomposition of the Ag2O leads to an improved oxygen stoichiometry in these samples. Electron irradiation is found to enhance the intragrain critical current densities, whereas the oxygen reduction leads to reduced intragrain currents. To determine the influence of the additions also on the intergrain critical current densities, standard four-point transport current measurements are carried out on the same samples. It is found that a maximum enhancement of the critical current density is obtained by the addition of 10 wt{\%} silver oxide; however, this critical current density is drastically reduced by applying small external magnetic fields. The lower critical field of the matrix and the corresponding Josephson penetration depth are determined from transport current measurements. The Ag2O additions and the green phase particles are found to separate the superconducting YBa2Cu3O7-δ grains. The resulting larger widths of the barriers between the superconducting grains are found to cause a stronger influence of external magnetic fields on the intergrain critical current densities.",
author = "Koblischka, {Michael Rudolf} and Th Schuster and H. Kronm{\"u}ller",
year = "1993",
month = "6",
day = "20",
doi = "10.1016/0921-4534(93)90133-B",
language = "English",
volume = "211",
pages = "263--278",
journal = "Physica C: Superconductivity and its Applications",
issn = "0921-4534",
publisher = "Elsevier",
number = "3-4",

}

TY - JOUR

T1 - Influence of additions and radiation damage on the superconducting properties of sintered YBa2Cu3O7 - gd

AU - Koblischka, Michael Rudolf

AU - Schuster, Th

AU - Kronmüller, H.

PY - 1993/6/20

Y1 - 1993/6/20

N2 - Using the high-resolution Faraday (HRF) technique, domain patterns of sintered YBa2Cu3O7 - δ samples containing additions of Ag2O and Y2BaCuO5 are obtained. Similar observations are carried out on sintered YBa2Cu3O7-δ samples with reduced oxygen content and on electron-irradiated samples. The penetration of flux into sintered high-Tc superconductors is found to be totally different from single crystalline materials (single crystals and epitaxial thin films) as the Abrikosov vortices penetrate the sample not as a whole thus forming a so-called flux front. Only a flux penetration into single superconducting grains is observed. From the measured flux density profiles, the intragrain critical current densities are determined locally. It is found that the chemical impurity phases do not affect the intragranular flux density distribution and the intragranular critical current density, but the decomposition of the Ag2O leads to an improved oxygen stoichiometry in these samples. Electron irradiation is found to enhance the intragrain critical current densities, whereas the oxygen reduction leads to reduced intragrain currents. To determine the influence of the additions also on the intergrain critical current densities, standard four-point transport current measurements are carried out on the same samples. It is found that a maximum enhancement of the critical current density is obtained by the addition of 10 wt% silver oxide; however, this critical current density is drastically reduced by applying small external magnetic fields. The lower critical field of the matrix and the corresponding Josephson penetration depth are determined from transport current measurements. The Ag2O additions and the green phase particles are found to separate the superconducting YBa2Cu3O7-δ grains. The resulting larger widths of the barriers between the superconducting grains are found to cause a stronger influence of external magnetic fields on the intergrain critical current densities.

AB - Using the high-resolution Faraday (HRF) technique, domain patterns of sintered YBa2Cu3O7 - δ samples containing additions of Ag2O and Y2BaCuO5 are obtained. Similar observations are carried out on sintered YBa2Cu3O7-δ samples with reduced oxygen content and on electron-irradiated samples. The penetration of flux into sintered high-Tc superconductors is found to be totally different from single crystalline materials (single crystals and epitaxial thin films) as the Abrikosov vortices penetrate the sample not as a whole thus forming a so-called flux front. Only a flux penetration into single superconducting grains is observed. From the measured flux density profiles, the intragrain critical current densities are determined locally. It is found that the chemical impurity phases do not affect the intragranular flux density distribution and the intragranular critical current density, but the decomposition of the Ag2O leads to an improved oxygen stoichiometry in these samples. Electron irradiation is found to enhance the intragrain critical current densities, whereas the oxygen reduction leads to reduced intragrain currents. To determine the influence of the additions also on the intergrain critical current densities, standard four-point transport current measurements are carried out on the same samples. It is found that a maximum enhancement of the critical current density is obtained by the addition of 10 wt% silver oxide; however, this critical current density is drastically reduced by applying small external magnetic fields. The lower critical field of the matrix and the corresponding Josephson penetration depth are determined from transport current measurements. The Ag2O additions and the green phase particles are found to separate the superconducting YBa2Cu3O7-δ grains. The resulting larger widths of the barriers between the superconducting grains are found to cause a stronger influence of external magnetic fields on the intergrain critical current densities.

UR - http://www.scopus.com/inward/record.url?scp=0027610208&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=0027610208&partnerID=8YFLogxK

U2 - 10.1016/0921-4534(93)90133-B

DO - 10.1016/0921-4534(93)90133-B

M3 - Article

VL - 211

SP - 263

EP - 278

JO - Physica C: Superconductivity and its Applications

JF - Physica C: Superconductivity and its Applications

SN - 0921-4534

IS - 3-4

ER -