Influence of carbon addition to Fe-Mn-Si type alloy on the structure and shape memory effect

Witold Prendota, Kamil Goc, Shunsuke Miyazawa, Akito Takasaki, Damian Rybicki, Czeslaw Kapusta

Research output: Contribution to journalArticle

Abstract

The study presented is focused on the influence of carbon addition on properties of the Fe-Mn-Si type intelligent materials with basic composition of Fe64Mn30Si6 (wt. %). Three alloys were prepared, starting from elemental powders, with 0, 0.1, and 0.3 wt. % of carbon, at corresponding silicon content reduction. For the synthesis, the mechanical alloying, sintering, and annealing were applied. Further process involved deformation and subsequent heating in a furnace. High temperature X-ray diffraction patterns, obtained at room temperature and up to 600°C, showed evolution of α′, γ, and ϵ phase peaks. The study revealed that a small carbon addition (of 0.1 wt. %), could increase shape recovery stress, even up to 1.8% after one cycle of training. The higher carbon content leads to a deterioration of the property. Also, relative density differences are observed between the sintered Fe64Mn30Si6 (wt. %) alloys with before/after annealing with/without mechanical alloying involvement.

Original languageEnglish
Article number6950876
JournalAdvances in Materials Science and Engineering
Volume2018
DOIs
Publication statusPublished - 2018 Jan 1

ASJC Scopus subject areas

  • Materials Science(all)
  • Engineering(all)

Fingerprint Dive into the research topics of 'Influence of carbon addition to Fe-Mn-Si type alloy on the structure and shape memory effect'. Together they form a unique fingerprint.

  • Cite this