Nondispersive hole transport in a spin-coated dendrimer film measured by the charge-generation-layer time-of-flight method

Jonathan P.J. Markham, Thomas D. Anthopoulos, Ifor D.W. Samuel, Gary J. Richards, Paul L. Burn, Chan Im, Heinz Bässler

Research output: Contribution to journalArticlepeer-review

33 Citations (Scopus)

Abstract

Measurements of the mobility of a first-generation (G1) bis-fluorene cored dendrimer have been performed on spin-coated samples of 500 nm thickness using the charge-generation-layer time-of-flight (TOF) technique. A 10 nm perylene charge generation layer was excited by the 532 nm line of a Q-switched Nd:YAG laser and the generated carriers swept through the dendrimer film under an applied field. We observe nondispersive hole transport in the dendrimer layer with a room-temperature mobility μ=2.0×10-4cm2/Vs at a field of 0.55 MV/cm. There is a weak field dependence of the mobility and it increases from μ=1.6×10-4cm2/Vs at 0.2 MV/cm to μ=3.0×10-4cm2/Vs at 1.4 MV/cm. These results suggest that the measurement of mobility by TOF in spin-coated samples on thickness scales relevant to organic light-emitting diodes can yield valuable information, and that dendrimers are promising materials for device applications.

Original languageEnglish
Pages (from-to)3266-3268
Number of pages3
JournalApplied Physics Letters
Volume81
Issue number17
DOIs
Publication statusPublished - 2002 Oct 21
Externally publishedYes

ASJC Scopus subject areas

  • Physics and Astronomy (miscellaneous)

Fingerprint

Dive into the research topics of 'Nondispersive hole transport in a spin-coated dendrimer film measured by the charge-generation-layer time-of-flight method'. Together they form a unique fingerprint.

Cite this