Potentials of RE-Ba2Cu3Oy in the silver base technology

M. Muralidhar, N. Sakai, T. Machi, I. Hirabayashi, S. Tanaka

Research output: Contribution to journalArticle

1 Citation (Scopus)

Abstract

With the aim to develop low cost, high performance superconducting thick films, we tested a new method, starting from a mixture of Er2BaO4, BaCuO2, and CuO in the stoichiometric Er-123 ratio. Thick films were prepared by the screen printing technique, spreading the mixture paste on silver and MgO single-crystalline substrates processed then in Ar-1% O2 atmosphere. Using a double-step annealing process, we obtained good quality Er-123 thick films on silver substrates, with Tc (onset) 92 K and transition width <1.5 K. Formation of large flat grains was observed by scanning electron microscope. Transmission electron microscopy observations showed clean and sharp interfaces between 123 phase and silver substrate.

Original languageEnglish
Pages (from-to)314-319
Number of pages6
JournalPhysica C: Superconductivity and its applications
Volume463-465
Issue numberSUPPL.
DOIs
Publication statusPublished - 2007 Oct 1

Keywords

  • Electron probe micro analysis
  • ErBaO
  • Quench experiments
  • SEM and TEM
  • Thick films
  • XRD

ASJC Scopus subject areas

  • Electronic, Optical and Magnetic Materials
  • Condensed Matter Physics
  • Energy Engineering and Power Technology
  • Electrical and Electronic Engineering

Fingerprint Dive into the research topics of 'Potentials of RE-Ba<sub>2</sub>Cu<sub>3</sub>O<sub>y</sub> in the silver base technology'. Together they form a unique fingerprint.

  • Cite this