Study on tribological properties of polyisobutylene lubricant for use in screw tightening

Takeftimi Otsu, Kyoichi Komatsu, Shinji Hashimura

Research output: Contribution to journalArticle

3 Citations (Scopus)

Abstract

The lubrication performance of polyisobutylene which is used as a lubricant for bolt tightening, was investigated in order to understand the lubrication mechanism during the tightening process. Ball on plate type spinning friction tests were conducted, and three kind of polyisobutylene(PIB-L, M, H) in which the highest viscosity is PIB-H, followed by PIB-M and PIB-L, and polyphenyl ether(5P4E) were used as lubricants in this study. Results show that the friction coefficient of PIB at initial stage of the tests at 400 MPa, depends on the viscosity, and that of PIB-H is the highest in the lubricants. It is also shown the friction coefficient increase with increasing contact pressure, and that of PIB-L, PIB-H and 5P4E at 600 MPa is greater than that of PIB-M. Large wear is observed on the contact surface after the test. In the spinning test, the thickness of entrapment oil film decrease with time, and the decreasing rate in 5P4E is greater than that in PIB-M. These results suggest that the lubrication film formed by PIB-M has an ability to prevent for wear and seizure at the condition with high contact pressure, such as the contact of screw tightening.

Original languageEnglish
Pages (from-to)866-873
Number of pages8
JournalToraibarojisuto/Journal of Japanese Society of Tribologists
Volume61
Issue number12
Publication statusPublished - 2016

Fingerprint

polyisobutylene
screws
lubricants
Lubrication
Lubricants
lubrication
Friction
Bolt tightening
Wear of materials
Viscosity
coefficient of friction
metal spinning
polyphenyl ether
viscosity
seizures
bolts
Ether
entrapment
Ethers
Oils

Keywords

  • Friction
  • Lubricant
  • Polyisobutylene
  • Polyphenyl ether
  • Screw

ASJC Scopus subject areas

  • Mechanics of Materials
  • Mechanical Engineering
  • Surfaces and Interfaces
  • Surfaces, Coatings and Films
  • Materials Chemistry

Cite this

Study on tribological properties of polyisobutylene lubricant for use in screw tightening. / Otsu, Takeftimi; Komatsu, Kyoichi; Hashimura, Shinji.

In: Toraibarojisuto/Journal of Japanese Society of Tribologists, Vol. 61, No. 12, 2016, p. 866-873.

Research output: Contribution to journalArticle

@article{ac06a55712d44d38a673ac4a3694d32b,
title = "Study on tribological properties of polyisobutylene lubricant for use in screw tightening",
abstract = "The lubrication performance of polyisobutylene which is used as a lubricant for bolt tightening, was investigated in order to understand the lubrication mechanism during the tightening process. Ball on plate type spinning friction tests were conducted, and three kind of polyisobutylene(PIB-L, M, H) in which the highest viscosity is PIB-H, followed by PIB-M and PIB-L, and polyphenyl ether(5P4E) were used as lubricants in this study. Results show that the friction coefficient of PIB at initial stage of the tests at 400 MPa, depends on the viscosity, and that of PIB-H is the highest in the lubricants. It is also shown the friction coefficient increase with increasing contact pressure, and that of PIB-L, PIB-H and 5P4E at 600 MPa is greater than that of PIB-M. Large wear is observed on the contact surface after the test. In the spinning test, the thickness of entrapment oil film decrease with time, and the decreasing rate in 5P4E is greater than that in PIB-M. These results suggest that the lubrication film formed by PIB-M has an ability to prevent for wear and seizure at the condition with high contact pressure, such as the contact of screw tightening.",
keywords = "Friction, Lubricant, Polyisobutylene, Polyphenyl ether, Screw",
author = "Takeftimi Otsu and Kyoichi Komatsu and Shinji Hashimura",
year = "2016",
language = "English",
volume = "61",
pages = "866--873",
journal = "Toraibarojisuto/Journal of Japanese Society of Tribologists",
issn = "0915-1168",
publisher = "Japanese Society of Tribologists",
number = "12",

}

TY - JOUR

T1 - Study on tribological properties of polyisobutylene lubricant for use in screw tightening

AU - Otsu, Takeftimi

AU - Komatsu, Kyoichi

AU - Hashimura, Shinji

PY - 2016

Y1 - 2016

N2 - The lubrication performance of polyisobutylene which is used as a lubricant for bolt tightening, was investigated in order to understand the lubrication mechanism during the tightening process. Ball on plate type spinning friction tests were conducted, and three kind of polyisobutylene(PIB-L, M, H) in which the highest viscosity is PIB-H, followed by PIB-M and PIB-L, and polyphenyl ether(5P4E) were used as lubricants in this study. Results show that the friction coefficient of PIB at initial stage of the tests at 400 MPa, depends on the viscosity, and that of PIB-H is the highest in the lubricants. It is also shown the friction coefficient increase with increasing contact pressure, and that of PIB-L, PIB-H and 5P4E at 600 MPa is greater than that of PIB-M. Large wear is observed on the contact surface after the test. In the spinning test, the thickness of entrapment oil film decrease with time, and the decreasing rate in 5P4E is greater than that in PIB-M. These results suggest that the lubrication film formed by PIB-M has an ability to prevent for wear and seizure at the condition with high contact pressure, such as the contact of screw tightening.

AB - The lubrication performance of polyisobutylene which is used as a lubricant for bolt tightening, was investigated in order to understand the lubrication mechanism during the tightening process. Ball on plate type spinning friction tests were conducted, and three kind of polyisobutylene(PIB-L, M, H) in which the highest viscosity is PIB-H, followed by PIB-M and PIB-L, and polyphenyl ether(5P4E) were used as lubricants in this study. Results show that the friction coefficient of PIB at initial stage of the tests at 400 MPa, depends on the viscosity, and that of PIB-H is the highest in the lubricants. It is also shown the friction coefficient increase with increasing contact pressure, and that of PIB-L, PIB-H and 5P4E at 600 MPa is greater than that of PIB-M. Large wear is observed on the contact surface after the test. In the spinning test, the thickness of entrapment oil film decrease with time, and the decreasing rate in 5P4E is greater than that in PIB-M. These results suggest that the lubrication film formed by PIB-M has an ability to prevent for wear and seizure at the condition with high contact pressure, such as the contact of screw tightening.

KW - Friction

KW - Lubricant

KW - Polyisobutylene

KW - Polyphenyl ether

KW - Screw

UR - http://www.scopus.com/inward/record.url?scp=85015389440&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=85015389440&partnerID=8YFLogxK

M3 - Article

AN - SCOPUS:85015389440

VL - 61

SP - 866

EP - 873

JO - Toraibarojisuto/Journal of Japanese Society of Tribologists

JF - Toraibarojisuto/Journal of Japanese Society of Tribologists

SN - 0915-1168

IS - 12

ER -