Synthesis of Mg2Ni alloy by bulk mechanical alloying

T. Aizawa, T. Kuji, H. Nakano

Research output: Contribution to journalArticle

69 Citations (Scopus)

Abstract

Mg2Ni was synthesized by a solid-state reaction from the constituent elemental powder mixtures via bulk mechanical alloying. Since homogeneous refining and alloying takes place efficiently by repeated forging, the process time can be reduced to one fiftieth of time duration necessary for conventional mechanical milling and attrition. This MA Mg2Ni alloy can be obtained as a high dense powder compact with a relative mass density in the order of 85%; its average powder particle size ranges from 1 to 3 μm. The prepared Mg2Ni alloy has a sufficiently high reaction rate to hydrogen even at relatively lower temperatures and a potential to form a ternary hydride on the pressure-composition isotherms from 523 to 623 K. The enthalpy and entropy for ternary hydride formation were estimated to be -28. 7 KJ/mole-H and -46.8 J/K/mole-H, respectively. The present bulk mechanical alloying was found to be adaptive to fabrication of single phase Mg2Ni in high productivity.

Original languageEnglish
Pages (from-to)248-253
Number of pages6
JournalJournal of Alloys and Compounds
Volume291
Issue number1-2
DOIs
Publication statusPublished - 1999 Sep 27

ASJC Scopus subject areas

  • Mechanics of Materials
  • Mechanical Engineering
  • Metals and Alloys
  • Materials Chemistry

Fingerprint Dive into the research topics of 'Synthesis of Mg<sub>2</sub>Ni alloy by bulk mechanical alloying'. Together they form a unique fingerprint.

  • Cite this