Synthesis of REBa2Cu3O7-∂ (RE=Nd, Eu, Gd) Nanoparticles by Wet-Mixing Method

W. G. Suharta, P. Suardana, W. Windaryoto, S. Pratapa, S. Suasmoro, D. Darminto, Yasuyuki Ishii, W. Isao

Research output: Contribution to journalConference article

1 Citation (Scopus)

Abstract

The Nd0.33Eu0.33Gd0.33Ba2Cu3O7-∂ (NEG-123) nanoparticles have been successfully synthesized by wet-mixing method using HNO3 as dissolving agent. The NEG-123 samples are divided into two which were treated differently. The first and second samples were mixed respectively, for one and 24 hours. All the samples were then calcined at 600°C for 3 hours, and sintered at relatively low temperature (750 to 900°C), each for 30 minutes. Samples were characterized using X-ray diffraction (XRD), transmission electron microscopy (TEM), and vibrating sample magnetometer (VSM). Rietveld analysis shows the lattice parameter of a-axis decreases with the increasing sintering temperature from 750 to 900°C, while the lattice parameter of b and c-axes increases. Further, it was known based on the XRD analysis that the higher the sintering temperature, the greater the peak intensities and average crystal size. The NEG-123 samples with the average crystal size of hundreds nanometer exhibit paramagnetism, while those with average crystal size of ten nanometers demonstrate superparamagnetism at room temperature.

Original languageEnglish
Article number012027
JournalJournal of Physics: Conference Series
Volume1091
Issue number1
DOIs
Publication statusPublished - 2018 Sep 20
Externally publishedYes
Event9th Seminar on Magnetic Materials, SMM 2015 - Palembang, South Sumatera, Indonesia
Duration: 2015 Oct 192015 Oct 21

Fingerprint

nanoparticles
synthesis
lattice parameters
sintering
crystals
paramagnetism
diffraction
magnetometers
dissolving
x rays
transmission electron microscopy
temperature
room temperature

ASJC Scopus subject areas

  • Physics and Astronomy(all)

Cite this

Suharta, W. G., Suardana, P., Windaryoto, W., Pratapa, S., Suasmoro, S., Darminto, D., ... Isao, W. (2018). Synthesis of REBa2Cu3O7-∂ (RE=Nd, Eu, Gd) Nanoparticles by Wet-Mixing Method. Journal of Physics: Conference Series, 1091(1), [012027]. https://doi.org/10.1088/1742-6596/1091/1/012027

Synthesis of REBa2Cu3O7-∂ (RE=Nd, Eu, Gd) Nanoparticles by Wet-Mixing Method. / Suharta, W. G.; Suardana, P.; Windaryoto, W.; Pratapa, S.; Suasmoro, S.; Darminto, D.; Ishii, Yasuyuki; Isao, W.

In: Journal of Physics: Conference Series, Vol. 1091, No. 1, 012027, 20.09.2018.

Research output: Contribution to journalConference article

Suharta, WG, Suardana, P, Windaryoto, W, Pratapa, S, Suasmoro, S, Darminto, D, Ishii, Y & Isao, W 2018, 'Synthesis of REBa2Cu3O7-∂ (RE=Nd, Eu, Gd) Nanoparticles by Wet-Mixing Method', Journal of Physics: Conference Series, vol. 1091, no. 1, 012027. https://doi.org/10.1088/1742-6596/1091/1/012027
Suharta WG, Suardana P, Windaryoto W, Pratapa S, Suasmoro S, Darminto D et al. Synthesis of REBa2Cu3O7-∂ (RE=Nd, Eu, Gd) Nanoparticles by Wet-Mixing Method. Journal of Physics: Conference Series. 2018 Sep 20;1091(1). 012027. https://doi.org/10.1088/1742-6596/1091/1/012027
Suharta, W. G. ; Suardana, P. ; Windaryoto, W. ; Pratapa, S. ; Suasmoro, S. ; Darminto, D. ; Ishii, Yasuyuki ; Isao, W. / Synthesis of REBa2Cu3O7-∂ (RE=Nd, Eu, Gd) Nanoparticles by Wet-Mixing Method. In: Journal of Physics: Conference Series. 2018 ; Vol. 1091, No. 1.
@article{b69591f3134646b8970a2e1e64b1bcf3,
title = "Synthesis of REBa2Cu3O7-∂ (RE=Nd, Eu, Gd) Nanoparticles by Wet-Mixing Method",
abstract = "The Nd0.33Eu0.33Gd0.33Ba2Cu3O7-∂ (NEG-123) nanoparticles have been successfully synthesized by wet-mixing method using HNO3 as dissolving agent. The NEG-123 samples are divided into two which were treated differently. The first and second samples were mixed respectively, for one and 24 hours. All the samples were then calcined at 600°C for 3 hours, and sintered at relatively low temperature (750 to 900°C), each for 30 minutes. Samples were characterized using X-ray diffraction (XRD), transmission electron microscopy (TEM), and vibrating sample magnetometer (VSM). Rietveld analysis shows the lattice parameter of a-axis decreases with the increasing sintering temperature from 750 to 900°C, while the lattice parameter of b and c-axes increases. Further, it was known based on the XRD analysis that the higher the sintering temperature, the greater the peak intensities and average crystal size. The NEG-123 samples with the average crystal size of hundreds nanometer exhibit paramagnetism, while those with average crystal size of ten nanometers demonstrate superparamagnetism at room temperature.",
author = "Suharta, {W. G.} and P. Suardana and W. Windaryoto and S. Pratapa and S. Suasmoro and D. Darminto and Yasuyuki Ishii and W. Isao",
year = "2018",
month = "9",
day = "20",
doi = "10.1088/1742-6596/1091/1/012027",
language = "English",
volume = "1091",
journal = "Journal of Physics: Conference Series",
issn = "1742-6588",
publisher = "IOP Publishing Ltd.",
number = "1",

}

TY - JOUR

T1 - Synthesis of REBa2Cu3O7-∂ (RE=Nd, Eu, Gd) Nanoparticles by Wet-Mixing Method

AU - Suharta, W. G.

AU - Suardana, P.

AU - Windaryoto, W.

AU - Pratapa, S.

AU - Suasmoro, S.

AU - Darminto, D.

AU - Ishii, Yasuyuki

AU - Isao, W.

PY - 2018/9/20

Y1 - 2018/9/20

N2 - The Nd0.33Eu0.33Gd0.33Ba2Cu3O7-∂ (NEG-123) nanoparticles have been successfully synthesized by wet-mixing method using HNO3 as dissolving agent. The NEG-123 samples are divided into two which were treated differently. The first and second samples were mixed respectively, for one and 24 hours. All the samples were then calcined at 600°C for 3 hours, and sintered at relatively low temperature (750 to 900°C), each for 30 minutes. Samples were characterized using X-ray diffraction (XRD), transmission electron microscopy (TEM), and vibrating sample magnetometer (VSM). Rietveld analysis shows the lattice parameter of a-axis decreases with the increasing sintering temperature from 750 to 900°C, while the lattice parameter of b and c-axes increases. Further, it was known based on the XRD analysis that the higher the sintering temperature, the greater the peak intensities and average crystal size. The NEG-123 samples with the average crystal size of hundreds nanometer exhibit paramagnetism, while those with average crystal size of ten nanometers demonstrate superparamagnetism at room temperature.

AB - The Nd0.33Eu0.33Gd0.33Ba2Cu3O7-∂ (NEG-123) nanoparticles have been successfully synthesized by wet-mixing method using HNO3 as dissolving agent. The NEG-123 samples are divided into two which were treated differently. The first and second samples were mixed respectively, for one and 24 hours. All the samples were then calcined at 600°C for 3 hours, and sintered at relatively low temperature (750 to 900°C), each for 30 minutes. Samples were characterized using X-ray diffraction (XRD), transmission electron microscopy (TEM), and vibrating sample magnetometer (VSM). Rietveld analysis shows the lattice parameter of a-axis decreases with the increasing sintering temperature from 750 to 900°C, while the lattice parameter of b and c-axes increases. Further, it was known based on the XRD analysis that the higher the sintering temperature, the greater the peak intensities and average crystal size. The NEG-123 samples with the average crystal size of hundreds nanometer exhibit paramagnetism, while those with average crystal size of ten nanometers demonstrate superparamagnetism at room temperature.

UR - http://www.scopus.com/inward/record.url?scp=85054503323&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=85054503323&partnerID=8YFLogxK

U2 - 10.1088/1742-6596/1091/1/012027

DO - 10.1088/1742-6596/1091/1/012027

M3 - Conference article

AN - SCOPUS:85054503323

VL - 1091

JO - Journal of Physics: Conference Series

JF - Journal of Physics: Conference Series

SN - 1742-6588

IS - 1

M1 - 012027

ER -