Tensile and bending mechanical properties of bulk superconductors at room temperature

K. Katagiri, A. Murakami, Y. Shoji, H. Teshima, M. Sawamura, A. Iwamoto, T. Mito, M. Murakami

Research output: Contribution to journalArticle

18 Citations (Scopus)

Abstract

Tensile and 3-point bending tests of specimens cut from an Y123 and a Gd123 bulk superconductors fabricated by using the modified QMG (Quench and Melt Growth) process were carried out at room temperature. The mechanical properties obtained by two testing method were compared. The average values of the Young's modulus obtained by tensile tests, 122 GPa for Y123 and 109 GPa for Gd123, were lower than those obtained by bending tests, 132 and 117 GPa, respectively. The average values of the tensile strength, 39 MPa for Y123 and 42 MPa for Gd123, were also lower than those of the bending strength, 74 MPa and 71 MPa, respectively. There was no appreciable difference between the Weibull coefficient for the tensile strength and that for the bending strength, 6.9, in Gd123. On the other hand, the coefficient for the bending strength, 17.6, was significantly higher than that for the tensile strength, 6.8, in Y123.

Original languageEnglish
Pages (from-to)633-637
Number of pages5
JournalPhysica C: Superconductivity and its applications
Volume412-414
Issue numberSPEC. ISS.
DOIs
Publication statusPublished - 2004 Oct 1

Keywords

  • Bending test
  • Bulk superconductor
  • Gd123
  • Tensile test
  • Y123

ASJC Scopus subject areas

  • Electronic, Optical and Magnetic Materials
  • Condensed Matter Physics
  • Energy Engineering and Power Technology
  • Electrical and Electronic Engineering

Fingerprint Dive into the research topics of 'Tensile and bending mechanical properties of bulk superconductors at room temperature'. Together they form a unique fingerprint.

  • Cite this

    Katagiri, K., Murakami, A., Shoji, Y., Teshima, H., Sawamura, M., Iwamoto, A., Mito, T., & Murakami, M. (2004). Tensile and bending mechanical properties of bulk superconductors at room temperature. Physica C: Superconductivity and its applications, 412-414(SPEC. ISS.), 633-637. https://doi.org/10.1016/j.physc.2003.12.067