A trial of FGM bearings with solid lubricant

T. Hashimoto, H. Kohri, Atsushi Yumoto, I. Shiota

研究成果: Conference contribution

抄録

It is difficult to use an ordinary plain bearing under a high load or at a high friction speed because lubricant oil is pushed out from the friction surface or deterioration of the lubricant oil is caused by heat of friction. A solid lubricant, MoS2, is promising in such condition. When the lubricant is dispersed in a matrix, the solid lubricant is always supplied from the matrix. Such a composite bearing needs a back metal to maintain its shape. The heat of friction may cause a crack between the bearing and the back metal due to thermal stress. A bearing with low coefficient of friction is necessary to decrease the heat of friction, and an FGM structure is also promising to decrease the stress. The aim of this experiment is to fabricate and to examine friction properties of the composites. Cu was plated on the lubricant particles by electroless deposition. The lubricant volume fraction (hereafter V f) was up to Vf 30 %. The Cu plated lubricant particles were hot-pressed to form a composite at 873 K under 30 MPa in a vacuum. Friction properties of the composites were determined by using a ball-on-disk type testing machine. The test was performed in the air without oil at room temperature. The solid lubricant in the composites was effective to decrease the coefficients of friction under a high load when the Vf was higher than 20 %.

元の言語English
ホスト出版物のタイトルMaterials Science Forum
ページ465-470
ページ数6
631-632
DOI
出版物ステータスPublished - 2010
外部発表Yes
イベント10th International Symposium on Multiscale, Multifunctional and Functionally Graded Materials, MM and FGMs - Sendai
継続期間: 2008 9 222008 9 25

出版物シリーズ

名前Materials Science Forum
631-632
ISSN(印刷物)02555476

Other

Other10th International Symposium on Multiscale, Multifunctional and Functionally Graded Materials, MM and FGMs
Sendai
期間08/9/2208/9/25

Fingerprint

Bearings (structural)
functionally gradient materials
solid lubricants
Solid lubricants
Functionally graded materials
lubricants
friction
Friction
Lubricants
composite materials
oils
Composite materials
Oils
heat
coefficient of friction
electroless deposition
Metals
matrices
thermal stresses
test equipment

ASJC Scopus subject areas

  • Materials Science(all)
  • Condensed Matter Physics
  • Mechanical Engineering
  • Mechanics of Materials

これを引用

Hashimoto, T., Kohri, H., Yumoto, A., & Shiota, I. (2010). A trial of FGM bearings with solid lubricant. : Materials Science Forum (巻 631-632, pp. 465-470). (Materials Science Forum; 巻数 631-632). https://doi.org/10.4028/www.scientific.net/MSF.631-632.465

A trial of FGM bearings with solid lubricant. / Hashimoto, T.; Kohri, H.; Yumoto, Atsushi; Shiota, I.

Materials Science Forum. 巻 631-632 2010. p. 465-470 (Materials Science Forum; 巻 631-632).

研究成果: Conference contribution

Hashimoto, T, Kohri, H, Yumoto, A & Shiota, I 2010, A trial of FGM bearings with solid lubricant. : Materials Science Forum. 巻. 631-632, Materials Science Forum, 巻. 631-632, pp. 465-470, 10th International Symposium on Multiscale, Multifunctional and Functionally Graded Materials, MM and FGMs, Sendai, 08/9/22. https://doi.org/10.4028/www.scientific.net/MSF.631-632.465
Hashimoto T, Kohri H, Yumoto A, Shiota I. A trial of FGM bearings with solid lubricant. : Materials Science Forum. 巻 631-632. 2010. p. 465-470. (Materials Science Forum). https://doi.org/10.4028/www.scientific.net/MSF.631-632.465
Hashimoto, T. ; Kohri, H. ; Yumoto, Atsushi ; Shiota, I. / A trial of FGM bearings with solid lubricant. Materials Science Forum. 巻 631-632 2010. pp. 465-470 (Materials Science Forum).
@inproceedings{f34d6da0f7f746b0a3e02fa4d4f6c60b,
title = "A trial of FGM bearings with solid lubricant",
abstract = "It is difficult to use an ordinary plain bearing under a high load or at a high friction speed because lubricant oil is pushed out from the friction surface or deterioration of the lubricant oil is caused by heat of friction. A solid lubricant, MoS2, is promising in such condition. When the lubricant is dispersed in a matrix, the solid lubricant is always supplied from the matrix. Such a composite bearing needs a back metal to maintain its shape. The heat of friction may cause a crack between the bearing and the back metal due to thermal stress. A bearing with low coefficient of friction is necessary to decrease the heat of friction, and an FGM structure is also promising to decrease the stress. The aim of this experiment is to fabricate and to examine friction properties of the composites. Cu was plated on the lubricant particles by electroless deposition. The lubricant volume fraction (hereafter V f) was up to Vf 30 {\%}. The Cu plated lubricant particles were hot-pressed to form a composite at 873 K under 30 MPa in a vacuum. Friction properties of the composites were determined by using a ball-on-disk type testing machine. The test was performed in the air without oil at room temperature. The solid lubricant in the composites was effective to decrease the coefficients of friction under a high load when the Vf was higher than 20 {\%}.",
keywords = "Composites, Electroless deposition, Friction, MoS, Wear",
author = "T. Hashimoto and H. Kohri and Atsushi Yumoto and I. Shiota",
year = "2010",
doi = "10.4028/www.scientific.net/MSF.631-632.465",
language = "English",
isbn = "0878493077",
volume = "631-632",
series = "Materials Science Forum",
pages = "465--470",
booktitle = "Materials Science Forum",

}

TY - GEN

T1 - A trial of FGM bearings with solid lubricant

AU - Hashimoto, T.

AU - Kohri, H.

AU - Yumoto, Atsushi

AU - Shiota, I.

PY - 2010

Y1 - 2010

N2 - It is difficult to use an ordinary plain bearing under a high load or at a high friction speed because lubricant oil is pushed out from the friction surface or deterioration of the lubricant oil is caused by heat of friction. A solid lubricant, MoS2, is promising in such condition. When the lubricant is dispersed in a matrix, the solid lubricant is always supplied from the matrix. Such a composite bearing needs a back metal to maintain its shape. The heat of friction may cause a crack between the bearing and the back metal due to thermal stress. A bearing with low coefficient of friction is necessary to decrease the heat of friction, and an FGM structure is also promising to decrease the stress. The aim of this experiment is to fabricate and to examine friction properties of the composites. Cu was plated on the lubricant particles by electroless deposition. The lubricant volume fraction (hereafter V f) was up to Vf 30 %. The Cu plated lubricant particles were hot-pressed to form a composite at 873 K under 30 MPa in a vacuum. Friction properties of the composites were determined by using a ball-on-disk type testing machine. The test was performed in the air without oil at room temperature. The solid lubricant in the composites was effective to decrease the coefficients of friction under a high load when the Vf was higher than 20 %.

AB - It is difficult to use an ordinary plain bearing under a high load or at a high friction speed because lubricant oil is pushed out from the friction surface or deterioration of the lubricant oil is caused by heat of friction. A solid lubricant, MoS2, is promising in such condition. When the lubricant is dispersed in a matrix, the solid lubricant is always supplied from the matrix. Such a composite bearing needs a back metal to maintain its shape. The heat of friction may cause a crack between the bearing and the back metal due to thermal stress. A bearing with low coefficient of friction is necessary to decrease the heat of friction, and an FGM structure is also promising to decrease the stress. The aim of this experiment is to fabricate and to examine friction properties of the composites. Cu was plated on the lubricant particles by electroless deposition. The lubricant volume fraction (hereafter V f) was up to Vf 30 %. The Cu plated lubricant particles were hot-pressed to form a composite at 873 K under 30 MPa in a vacuum. Friction properties of the composites were determined by using a ball-on-disk type testing machine. The test was performed in the air without oil at room temperature. The solid lubricant in the composites was effective to decrease the coefficients of friction under a high load when the Vf was higher than 20 %.

KW - Composites

KW - Electroless deposition

KW - Friction

KW - MoS

KW - Wear

UR - http://www.scopus.com/inward/record.url?scp=75849144959&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=75849144959&partnerID=8YFLogxK

U2 - 10.4028/www.scientific.net/MSF.631-632.465

DO - 10.4028/www.scientific.net/MSF.631-632.465

M3 - Conference contribution

AN - SCOPUS:75849144959

SN - 0878493077

SN - 9780878493074

VL - 631-632

T3 - Materials Science Forum

SP - 465

EP - 470

BT - Materials Science Forum

ER -