For Rare Earth-Transition Metal-Al with high undercooled liquid formability and glass-forming ability, bulk alloys have been produced with gas jet flow type electromagnetic levitation process, which is a new containerless process. A series of alloys of La 80-xCu 10Ni 5Co 5Al x, (x= 15, 20, 25 at%) were analyzed with respects to the supercooled solidification process, nucleation behavior of a crystalline phase, and the possibility of the formation of bulk amorphous alloys. In addition, the similar studies were carried out for the specimens containing SiC, which is reported to be effective to enlarge undercooling when used in the containerless process. The results show that the addition of SiC suppresses the nucleation of a crystalline phase, and thus, the undercooling T) increases in the range of δ T= 0.22 to 0.28 T m where T m is the melting point. In addition, partially crystallized bulk amorphous alloys with a diameter of 6 mm are obtainable for the alloys with 0.2 mass% SiC addition when they are solidified at approximate cooling rate of 100 K/s. Furthermore, the SiC free alloys of La 65Cu 10,Ni 5Co 5Al 15 and Nd 60Fe 20Co 10Al 10 are also obtainable as partially crystallized bulk amorphous alloys.
|ジャーナル||Nippon Kinzoku Gakkaishi/Journal of the Japan Institute of Metals|
|出版物ステータス||Published - 2006 2 1|
ASJC Scopus subject areas
- Condensed Matter Physics
- Mechanics of Materials
- Metals and Alloys
- Materials Chemistry