Chemical tuning of TiO2 nanoparticles and sintered compacts for enhanced thermoelectric properties

Chengyan Liu, Lei Miao, Jianhua Zhou, Rong Huang, Craig A.J. Fisher, Sakae Tanemura

研究成果: Article査読

37 被引用数 (Scopus)

抄録

A novel, fast combustion method for synthesizing anatase TiO2 nanoparticles (average diameter ∼14 nm) codoped with N and Nb in a single step is reported. XRD, STEM-EDX, and XPS measurements confirm that Nb ions are incorporated into the tetragonal lattice on Ti sites, while N ions occupy O sites, and likely also interstitial sites. Sintering of pellets of codoped powders under reducing conditions produced polycrystalline samples with the rutile structure. Chemically tuned samples have power factors up to 9.87 × 10-4 W m-1 K-2, 7 times higher than that of pure TiO2 sintered under the same conditions. In addition, the thermal conductivity is considerably lower at 2.6-4.0 W m-1 K -1 as a result of greater grain-boundary and point-defect scattering. The figure of merit, ZT, is improved to 0.35 at 700 C, which is the highest value reported for a TiO2 material to date, and is comparable to the highest values of any n-type thermoelectric oxide. Our material also exhibits good thermal stability in a pure N2 atmosphere and is an excellent candidate for thermoelectric power generators. Consequently, the combustion technique represents a promising new strategy for preparing foreign-atom-doped metal oxides; the chemical tuning approach, a combination of foreign-atom-doped nanoparticle synthesis and optimized sintering process, can be applied to prepare superior thermoelectric materials.

本文言語English
ページ(範囲)11487-11497
ページ数11
ジャーナルJournal of Physical Chemistry C
117
22
DOI
出版ステータスPublished - 2013 6月 6
外部発表はい

ASJC Scopus subject areas

  • 電子材料、光学材料、および磁性材料
  • エネルギー(全般)
  • 物理化学および理論化学
  • 表面、皮膜および薄膜

フィンガープリント

「Chemical tuning of TiO2 nanoparticles and sintered compacts for enhanced thermoelectric properties」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル