Corrosion performance of zinc-rich paints (ZRP) on mild steel in NaCl solution

Azizul H. Sofian, A. Tanaka, Kazuhiko Noda

研究成果: Conference contribution

抄録

Zinc rich paints (ZRP) are one of the most effective coatings used to protect steel from corrosion and they have been studied under severe environment like sea water, marine and industrial environments. Classic solvent based paint contributes to the increasing of harmful volatile organic compounds (VOC) to the environment have been a major problem. Here we focus on the corrosion behavior of an epoxy based ZRP with less organic solvent so they keep on with environment standards was studied. In this work, metal substrate was coated with 1, 3 and 5 coatings of ZRP and the cross section of the coating was observed by means of scanning electron microscopy (SEM). Electrochemical behaviors were compared, using potential corrosion measurement system.

元の言語English
ホスト出版物のタイトルECS Transactions
ページ17-24
ページ数8
45
エディション19
DOI
出版物ステータスPublished - 2013
イベントSymposium on Corrosion General Session - 221st ECS Meeting - Seattle, WA
継続期間: 2012 5 62012 5 10

Other

OtherSymposium on Corrosion General Session - 221st ECS Meeting
Seattle, WA
期間12/5/612/5/10

Fingerprint

Paint
Carbon steel
Zinc
Corrosion
Coatings
Volatile organic compounds
Organic solvents
Scanning electron microscopy
Steel
Substrates
Metals
Water

ASJC Scopus subject areas

  • Engineering(all)

これを引用

Corrosion performance of zinc-rich paints (ZRP) on mild steel in NaCl solution. / Sofian, Azizul H.; Tanaka, A.; Noda, Kazuhiko.

ECS Transactions. 巻 45 19. 編 2013. p. 17-24.

研究成果: Conference contribution

Sofian, AH, Tanaka, A & Noda, K 2013, Corrosion performance of zinc-rich paints (ZRP) on mild steel in NaCl solution. : ECS Transactions. 19 Edn, 巻. 45, pp. 17-24, Symposium on Corrosion General Session - 221st ECS Meeting, Seattle, WA, 12/5/6. https://doi.org/10.1149/04519.0017ecst
Sofian, Azizul H. ; Tanaka, A. ; Noda, Kazuhiko. / Corrosion performance of zinc-rich paints (ZRP) on mild steel in NaCl solution. ECS Transactions. 巻 45 19. 版 2013. pp. 17-24
@inproceedings{22e0ef046f9d4360aae374e1e7591e80,
title = "Corrosion performance of zinc-rich paints (ZRP) on mild steel in NaCl solution",
abstract = "Zinc rich paints (ZRP) are one of the most effective coatings used to protect steel from corrosion and they have been studied under severe environment like sea water, marine and industrial environments. Classic solvent based paint contributes to the increasing of harmful volatile organic compounds (VOC) to the environment have been a major problem. Here we focus on the corrosion behavior of an epoxy based ZRP with less organic solvent so they keep on with environment standards was studied. In this work, metal substrate was coated with 1, 3 and 5 coatings of ZRP and the cross section of the coating was observed by means of scanning electron microscopy (SEM). Electrochemical behaviors were compared, using potential corrosion measurement system.",
author = "Sofian, {Azizul H.} and A. Tanaka and Kazuhiko Noda",
year = "2013",
doi = "10.1149/04519.0017ecst",
language = "English",
isbn = "9781623320355",
volume = "45",
pages = "17--24",
booktitle = "ECS Transactions",
edition = "19",

}

TY - GEN

T1 - Corrosion performance of zinc-rich paints (ZRP) on mild steel in NaCl solution

AU - Sofian, Azizul H.

AU - Tanaka, A.

AU - Noda, Kazuhiko

PY - 2013

Y1 - 2013

N2 - Zinc rich paints (ZRP) are one of the most effective coatings used to protect steel from corrosion and they have been studied under severe environment like sea water, marine and industrial environments. Classic solvent based paint contributes to the increasing of harmful volatile organic compounds (VOC) to the environment have been a major problem. Here we focus on the corrosion behavior of an epoxy based ZRP with less organic solvent so they keep on with environment standards was studied. In this work, metal substrate was coated with 1, 3 and 5 coatings of ZRP and the cross section of the coating was observed by means of scanning electron microscopy (SEM). Electrochemical behaviors were compared, using potential corrosion measurement system.

AB - Zinc rich paints (ZRP) are one of the most effective coatings used to protect steel from corrosion and they have been studied under severe environment like sea water, marine and industrial environments. Classic solvent based paint contributes to the increasing of harmful volatile organic compounds (VOC) to the environment have been a major problem. Here we focus on the corrosion behavior of an epoxy based ZRP with less organic solvent so they keep on with environment standards was studied. In this work, metal substrate was coated with 1, 3 and 5 coatings of ZRP and the cross section of the coating was observed by means of scanning electron microscopy (SEM). Electrochemical behaviors were compared, using potential corrosion measurement system.

UR - http://www.scopus.com/inward/record.url?scp=84885732977&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=84885732977&partnerID=8YFLogxK

U2 - 10.1149/04519.0017ecst

DO - 10.1149/04519.0017ecst

M3 - Conference contribution

AN - SCOPUS:84885732977

SN - 9781623320355

VL - 45

SP - 17

EP - 24

BT - ECS Transactions

ER -