Corrosion resistance of composite oxide film prepared on Ca-added flame-resistant magnesium alloy AZCa612 by micro-arc oxidation

Oi Lun Li, Mika Tsunakawa, Yuta Shimada, Kae Nakamura, Kazuhito Nishinaka, Takahiro Ishizaki

研究成果: Article

11 引用 (Scopus)

抜粋

A composite oxide film was prepared on a flame-resistant magnesium alloy AZCa612 by micro-arc oxidation (MAO). The thickness of the film was approximately 30. μm, where the film was composed of mainly of MgO and Mg-Mn-Al oxide. Potentiodynamic polarization curve measurements demonstrated that the corrosion current density of the composite oxide film coated AZCa612 decreased by 6 orders of magnitude compared to bare substrate. Immersion tests in 5. wt.% NaCl solution after 42. day indicated the coating phase did not change significantly, which proved that the MAO coating have superior corrosion resistance in 5. wt.% NaCl aqueous solution.

元の言語English
ジャーナルCorrosion Science
DOI
出版物ステータスAccepted/In press - 2016 12 8

ASJC Scopus subject areas

  • Chemistry(all)
  • Chemical Engineering(all)
  • Materials Science(all)

フィンガープリント Corrosion resistance of composite oxide film prepared on Ca-added flame-resistant magnesium alloy AZCa612 by micro-arc oxidation' の研究トピックを掘り下げます。これらはともに一意のフィンガープリントを構成します。

  • これを引用