Crystallization and magnetic property of iron oxide nanoparticles precipitated in silica glass matrix

Y. Masubuchi, Y. Sato, A. Sawada, T. Motohashi, H. Kiyono, S. Kikkawa

研究成果: Article

17 引用 (Scopus)

抜粋

Crystallization and magnetic property of Fe2O3 nanoparticle precipitated in SiO2 matrix was investigated. Fe2O3/SiO2 nanocomposite thin film was obtained by annealing of the amorphous Fe-Si-O thin film deposited by RF-magnetron sputtering of (α-Fe2O3)1-x/(SiO2)x composite targets. The Fe2O3 crystallite size increased with decreasing SiO2 area ratio, x of the target and increasing annealing temperature. e{open}-Fe2O3 with the crystallite size of 20-30nm was obtained after annealing the film deposited in SiO2 area ratio, x=0.33-0.42 at 900°C. Lower SiO2 area ratio (x) than 0.25 and higher annealing temperature resulted in precipitation of α-Fe2O3 with the larger crystallite size than 40nm. In the case of SiO2 area ratio, x≥0.50, the annealed film was amorphous and showed higher magnetization and smaller coercivity due to the precipitation of very small crystalline γ-Fe2O3. The e{open}-Fe2O3/SiO2 composite thin film showed ferromagnetic hysteresis with coercive force of 0.14T.

元の言語English
ページ(範囲)2459-2462
ページ数4
ジャーナルJournal of the European Ceramic Society
31
発行部数14
DOI
出版物ステータスPublished - 2011 11

ASJC Scopus subject areas

  • Ceramics and Composites
  • Materials Chemistry

フィンガープリント Crystallization and magnetic property of iron oxide nanoparticles precipitated in silica glass matrix' の研究トピックを掘り下げます。これらはともに一意のフィンガープリントを構成します。

  • これを引用