Effect of Ambient gas and temperature on crystallization of boron nitride spheres prepared by vapor phase pyrolysis of Ammonia Borane

Yuting Wang, Yasunori Yamamoto, Hajime Kiyono, Shiro Shimada

研究成果: Article

13 引用 (Scopus)

抜粋

Synthesis of boron nitride spheres (BNS) was achieved by vapor phase pyrolysis of ammonia borane (BH3NH3) using two independently temperature-controlled furnaces in a glove box filled with N 2. The BNS were heated at 1300°-1700°C in flowing NH 3, N2, or Ar by multistep heat treatment. The sizes of the BNS could be controlled by heating BH3NH3 at different rates (1°C/min: 300-800 nm, 5°C/min: 300 nm-1.2 μm and 10°C/min: 300 nm-1.8 μm). The microstructures of BNS heated in different ambient gases were observed using transmission electron microscopy with selected area electron diffraction. NH3 gas produced BNS with well-crystallized surface shells and amorphous cores whereas N2 and Ar gases crystallized the entire BNS. It is evident that of these three ambient gases (NH3, N2, and Ar), N2 gas significantly enhances the crystallization of BN with randomly oriented grains.

元の言語English
ページ(範囲)787-792
ページ数6
ジャーナルJournal of the American Ceramic Society
92
発行部数4
DOI
出版物ステータスPublished - 2009 4

ASJC Scopus subject areas

  • Ceramics and Composites
  • Materials Chemistry

フィンガープリント Effect of Ambient gas and temperature on crystallization of boron nitride spheres prepared by vapor phase pyrolysis of Ammonia Borane' の研究トピックを掘り下げます。これらはともに一意のフィンガープリントを構成します。

  • これを引用