EFFECT OF DELTA FERRITE ON LOW TEMPERATURE TOUGHNESS OF TYPE 308L WELD METAL.

Tadao Onzawa, Akito Takasaki, Takashi Harada, Hiroshi Tamura

研究成果: Article

抄録

In this study, a relation on molybdenum-free weld metal (Type 308L) was investigated in detail by using transmission electron microscopy (TEM) and an analytical electron microscopy (STEM/EDX). From notch toughness test at 77K of as-welded metal, the toughness decreased monotonously and slightly with increasing amount of delta ferrite. This result differed from the previous data of Type 316L weld metal and revealed that toughness of Type 308L weld metal was basically unaffected by solidification mode. In eutectic delta ferrite, a loss of coherency between crystallographic orientation of delta ferrite and that of adjacent austenite matrix reduced as compared with previous data of Type 316L weld metal. Moreover, STEM/EDX analysis suggested that chromium content within eutectic delta ferrite was about 4 percent more than that within primary delta ferrite. This was considered to be due to difference of solidification mode.

元の言語English
ページ(範囲)81-85
ページ数5
ジャーナルYosetsu Gakkai Ronbunshu/Quarterly Journal of the Japan Welding Society
5
発行部数4
出版物ステータスPublished - 1987 11
外部発表Yes

Fingerprint

Toughness
Ferrite
Welds
Metals
Eutectics
Solidification
Energy dispersive spectroscopy
Temperature
Molybdenum
Chromium
Austenite
Electron microscopy
Transmission electron microscopy

ASJC Scopus subject areas

  • Mechanical Engineering

これを引用

EFFECT OF DELTA FERRITE ON LOW TEMPERATURE TOUGHNESS OF TYPE 308L WELD METAL. / Onzawa, Tadao; Takasaki, Akito; Harada, Takashi; Tamura, Hiroshi.

:: Yosetsu Gakkai Ronbunshu/Quarterly Journal of the Japan Welding Society, 巻 5, 番号 4, 11.1987, p. 81-85.

研究成果: Article

@article{dd534d8bb4f84836a21684abda08ec5d,
title = "EFFECT OF DELTA FERRITE ON LOW TEMPERATURE TOUGHNESS OF TYPE 308L WELD METAL.",
abstract = "In this study, a relation on molybdenum-free weld metal (Type 308L) was investigated in detail by using transmission electron microscopy (TEM) and an analytical electron microscopy (STEM/EDX). From notch toughness test at 77K of as-welded metal, the toughness decreased monotonously and slightly with increasing amount of delta ferrite. This result differed from the previous data of Type 316L weld metal and revealed that toughness of Type 308L weld metal was basically unaffected by solidification mode. In eutectic delta ferrite, a loss of coherency between crystallographic orientation of delta ferrite and that of adjacent austenite matrix reduced as compared with previous data of Type 316L weld metal. Moreover, STEM/EDX analysis suggested that chromium content within eutectic delta ferrite was about 4 percent more than that within primary delta ferrite. This was considered to be due to difference of solidification mode.",
author = "Tadao Onzawa and Akito Takasaki and Takashi Harada and Hiroshi Tamura",
year = "1987",
month = "11",
language = "English",
volume = "5",
pages = "81--85",
journal = "Yosetsu Gakkai Ronbunshu/Quarterly Journal of the Japan Welding Society",
issn = "0288-4771",
publisher = "Japan Welding Society",
number = "4",

}

TY - JOUR

T1 - EFFECT OF DELTA FERRITE ON LOW TEMPERATURE TOUGHNESS OF TYPE 308L WELD METAL.

AU - Onzawa, Tadao

AU - Takasaki, Akito

AU - Harada, Takashi

AU - Tamura, Hiroshi

PY - 1987/11

Y1 - 1987/11

N2 - In this study, a relation on molybdenum-free weld metal (Type 308L) was investigated in detail by using transmission electron microscopy (TEM) and an analytical electron microscopy (STEM/EDX). From notch toughness test at 77K of as-welded metal, the toughness decreased monotonously and slightly with increasing amount of delta ferrite. This result differed from the previous data of Type 316L weld metal and revealed that toughness of Type 308L weld metal was basically unaffected by solidification mode. In eutectic delta ferrite, a loss of coherency between crystallographic orientation of delta ferrite and that of adjacent austenite matrix reduced as compared with previous data of Type 316L weld metal. Moreover, STEM/EDX analysis suggested that chromium content within eutectic delta ferrite was about 4 percent more than that within primary delta ferrite. This was considered to be due to difference of solidification mode.

AB - In this study, a relation on molybdenum-free weld metal (Type 308L) was investigated in detail by using transmission electron microscopy (TEM) and an analytical electron microscopy (STEM/EDX). From notch toughness test at 77K of as-welded metal, the toughness decreased monotonously and slightly with increasing amount of delta ferrite. This result differed from the previous data of Type 316L weld metal and revealed that toughness of Type 308L weld metal was basically unaffected by solidification mode. In eutectic delta ferrite, a loss of coherency between crystallographic orientation of delta ferrite and that of adjacent austenite matrix reduced as compared with previous data of Type 316L weld metal. Moreover, STEM/EDX analysis suggested that chromium content within eutectic delta ferrite was about 4 percent more than that within primary delta ferrite. This was considered to be due to difference of solidification mode.

UR - http://www.scopus.com/inward/record.url?scp=0023450650&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=0023450650&partnerID=8YFLogxK

M3 - Article

AN - SCOPUS:0023450650

VL - 5

SP - 81

EP - 85

JO - Yosetsu Gakkai Ronbunshu/Quarterly Journal of the Japan Welding Society

JF - Yosetsu Gakkai Ronbunshu/Quarterly Journal of the Japan Welding Society

SN - 0288-4771

IS - 4

ER -