Effect of Graphene Nanoparticles Addition on Superconductivity of YBa2Cu3O7~δ Synthesized via the Thermal Treatment Method

Aliah Nursyahirah Kamarudin, Mohd Mustafa Awang Kechik, Siti Nabilah Abdullah, Hussein Baqiah, Soo Kien Chen, Muhammad Khalis Abdul Karim, Aima Ramli, Kean Pah Lim, Abdul Halim Shaari, Muralidhar Miryala, Masato Murakami, Zainal Abidin Talib

研究成果: Article査読

抄録

The development of high-temperature superconductor (HTS) YBa2Cu3O7~δ (Y123) bulks in industrial applications were established years ago. It is one of the developments that currently attracts great attention especially in transportation, superconductor cables and wires. This study is focused on the preparation of the Y123 bulk superconductors by the thermal treatment method due to the promising ways to develop high-quality Y123 superconductors with its simplicity, low cost, and relatively low reaction temperature used during the process. Y123 were added with graphene nanoparticles (x = (0.0–1.0) wt.%). Samples were then characterized by X-ray diffraction (XRD) analysis, field-emission scanning electron microscopy (FESEM), energy-dispersive X-ray spectroscopy (EDX), and alternating current susceptibility (ACS). It was found that Y123 confirmed that the majority of phases in all the XRD patterns was the orthorhombic crystal structure and the Pmmm space group with secondary phases belonged to Y2Ba1Cu1O5 (Y211). The highest Tc obtained when graphene nanoparticles were added in the Y123 sample was x = 1.0 wt.%, followed by x = 0.5 wt.% with 92.64 and 92.59 K, respectively. From the microstructure analysis, the average grain size significantly decreased to 4.754 µm at x = 0.5 wt.%. The addition of graphene nanoparticles had disturbed the grain growth of Y123, affecting the superconducting properties of the samples. On the other hand, the intergranular critical current density, Jcm, was found to increase with graphene nanoparticle addition and had the highest value at x = 1.0 wt.%, indicating that graphene nanoparticles acted as pinning centers in the Y123 matrix.

本文言語English
論文番号91
ジャーナルCoatings
12
1
DOI
出版ステータスPublished - 2022 1月

ASJC Scopus subject areas

  • 表面および界面
  • 表面、皮膜および薄膜
  • 材料化学

フィンガープリント

「Effect of Graphene Nanoparticles Addition on Superconductivity of YBa2Cu3O7~δ Synthesized via the Thermal Treatment Method」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル