TY - JOUR
T1 - EFFECT OF HEAT TREATMENTS ON THE MECHANICAL PROPERTIES OF A 6% Mn CRYOGENIC STEEL.
AU - Murakami, Masato
AU - Harada, Masahide
AU - Shibata, Koji
AU - Fujita, Toshio
PY - 1983/1/1
Y1 - 1983/1/1
N2 - The material was austenitized at 800 degree C for 1h and then either reheated 1h at 300-700 degree C (designated as QT), or intercritically heated at 650-725 degree C and reheated at 500-650 degree C (designated as QLT). The specimens were subjected to Charpy impact tests and tensile tests at minus 196 degree C. X-ray diffraction was used to determine the amount of retained austenite.
AB - The material was austenitized at 800 degree C for 1h and then either reheated 1h at 300-700 degree C (designated as QT), or intercritically heated at 650-725 degree C and reheated at 500-650 degree C (designated as QLT). The specimens were subjected to Charpy impact tests and tensile tests at minus 196 degree C. X-ray diffraction was used to determine the amount of retained austenite.
UR - http://www.scopus.com/inward/record.url?scp=0020779809&partnerID=8YFLogxK
UR - http://www.scopus.com/inward/citedby.url?scp=0020779809&partnerID=8YFLogxK
M3 - Conference article
AN - SCOPUS:0020779809
VL - 23
SP - b255
JO - Transactions of the Iron and Steel Institute of Japan
JF - Transactions of the Iron and Steel Institute of Japan
SN - 0915-1559
IS - 7
T2 - Prepr for the ISIJ Meet, 105th
Y2 - 1 April 1983 through 3 April 1983
ER -