Effect of UV irradiation on the shear bond strength of titanium with segmented polyurethane through γ-mercapto propyl trimethoxysilane

Harumi Sakamoto, Yohei Hirohashi, Hisashi Doi, Yusuke Tsutsumi, Yoshiaki Suzuki, Kazuhiko Noda, Takao Hanawa

研究成果: Article

7 引用 (Scopus)

抜粋

The objective of this study was to investigate the effect of UV irradiation on shear bond strength between a titanium (Ti) and a segmented polyurethane (SPU) composite through γ-mercapto propyl trimethoxysilane (γ-MPS). To this end, the shear bond strength of Ti/SPU interface of Ti-SPU composite under varying conditions of ultraviolet ray (UV) irradiation was evaluated by a shear bond test. The glass transition temperatures of SPU with and without UV irradiation were also determined using differential scanning calorimetry. It was found that the shear bond strength of Ti/SPU interface increased with UV irradiation. However, excessive UV irradiation decreased the shear bond strength of Ti/SPU interface. Glass transition temperature was found to increase during 40-60 seconds of UV irradiation. In terms of durability after immersion in water at 37°C for 30 days, shear bond strength was found to improve with UV irradiation. In conclusion, UV irradiation to a Ti-SPU composite was clearly one of the means to improve the shear bond strength of Ti/SPU interface.

元の言語English
ページ(範囲)124-132
ページ数9
ジャーナルDental Materials Journal
27
発行部数1
DOI
出版物ステータスPublished - 2008 7 9

    フィンガープリント

ASJC Scopus subject areas

  • Ceramics and Composites
  • Dentistry(all)

これを引用