Effects of second phase and platinum additions on the microstructure and the critical current density of OCMG processed (Nd, Eu, Gd)-Ba-Cu-O

M. Muralidhar, T. Saitoh, K. Segawa, M. Murakami

研究成果: Article

18 引用 (Scopus)

抜粋

We have investigated the effects of second phase (Nd, Eu, Gd)2BaCuO5 (NEG211) and platinum addition on the superconducting properties for (Nd, Eu, Gd)Ba2CUsOy (NEG123) composite prepared by the oxygen-controlled melt-growth (OCMG) process. The addition of NEG211 slightly decreased the critical temperature (Tc) and increased the critical current density (Jc), particularly in a low field region. The secondary peak effect, which is commonly observed in OCMG processed Nd123, was reduced with the NEG211 addition of >10%. Refinement of the NEG211 second phase was achieved by Pt addition, which led to a dramatic increase in both Jc values and the irreversibility field. Low field Jc varied as Vf/d, where Vfis the volume fraction and d is the mean diameter of NEG211, supporting the idea that the 211/123 matrix is responsible for the pinning-like melt-processed Y-Ba-Cu -O. However, in a high field region, due to the presence of additional pinning by field-induced pinning centers, such a relationship is not observed. Our results suggests that fine distribution of the second phase is effective in improving pinning properties in the (Nd, Eu, Gd)-Ba-Cu-O composite.

元の言語English
ページ(範囲)535-546
ページ数12
ジャーナルApplied Superconductivity
4
発行部数10-11
DOI
出版物ステータスPublished - 1996 10 1

ASJC Scopus subject areas

  • Engineering(all)
  • Physics and Astronomy(all)

フィンガープリント Effects of second phase and platinum additions on the microstructure and the critical current density of OCMG processed (Nd, Eu, Gd)-Ba-Cu-O' の研究トピックを掘り下げます。これらはともに一意のフィンガープリントを構成します。

  • これを引用