Fabrication of thick YBa2Cu3O7-x films on optimized SrTiO3 buffered-MgO single crystals

Paolo Mele, K. Matsumoto, T. Horide, A. Ichinose, M. Mukaida, Y. Yoshida, S. Horii

研究成果: Article

3 引用 (Scopus)

抄録

In this work, we studied the optimum deposition conditions for SrTiO 3 (STO) buffers deposited on MgO single crystals substrates by PLD method. We found that 120 nm thick STO films, deposited at 730 °C, present the smoothest surface and a minimum FWMH of the (002) reflection. High quality, smooth and free-crack YBa2Cu3O7-x (YBCO) thick superconducting films have then been fabricated using a deposition temperature of 800 °C on STO-buffered MgO substrates. A 373 nm thick YBCO/STO/MgO film can carry current densities Jc (77 K, 0 T) of 1.4 MA/cm2 and Jc (77 K, 5 T) of 0.14 MA/cm2. The Jc in high field overcomes the current transported in same experimental conditions by 180 nm thick YBCO film grown on Y2O3-decorated STO single crystal. For 1350 nm thick YBCO/STO/MgO film the Jc (77 K, 0 T) is about 0.8 MA/cm2 and Jc (77 K, 5 T) is 0.09 MA/cm 2.

元の言語English
ページ(範囲)3713-3716
ページ数4
ジャーナルIEEE Transactions on Applied Superconductivity
17
発行部数2
DOI
出版物ステータスPublished - 2007 6 1
外部発表Yes

Fingerprint

Single crystals
Fabrication
fabrication
single crystals
Superconducting films
superconducting films
Substrates
Pulsed laser deposition
Thick films
Buffers
Current density
cracks
buffers
current density
Cracks
strontium titanium oxide
barium copper yttrium oxide
Temperature
temperature
1-dodecylpyridoxal

ASJC Scopus subject areas

  • Electrical and Electronic Engineering
  • Physics and Astronomy (miscellaneous)

これを引用

Fabrication of thick YBa2Cu3O7-x films on optimized SrTiO3 buffered-MgO single crystals. / Mele, Paolo; Matsumoto, K.; Horide, T.; Ichinose, A.; Mukaida, M.; Yoshida, Y.; Horii, S.

:: IEEE Transactions on Applied Superconductivity, 巻 17, 番号 2, 01.06.2007, p. 3713-3716.

研究成果: Article

Mele, P, Matsumoto, K, Horide, T, Ichinose, A, Mukaida, M, Yoshida, Y & Horii, S 2007, 'Fabrication of thick YBa2Cu3O7-x films on optimized SrTiO3 buffered-MgO single crystals', IEEE Transactions on Applied Superconductivity, 巻. 17, 番号 2, pp. 3713-3716. https://doi.org/10.1109/TASC.2007.897422
Mele, Paolo ; Matsumoto, K. ; Horide, T. ; Ichinose, A. ; Mukaida, M. ; Yoshida, Y. ; Horii, S. / Fabrication of thick YBa2Cu3O7-x films on optimized SrTiO3 buffered-MgO single crystals. :: IEEE Transactions on Applied Superconductivity. 2007 ; 巻 17, 番号 2. pp. 3713-3716.
@article{d971c08bc2ab42cfbc8408e763821bf6,
title = "Fabrication of thick YBa2Cu3O7-x films on optimized SrTiO3 buffered-MgO single crystals",
abstract = "In this work, we studied the optimum deposition conditions for SrTiO 3 (STO) buffers deposited on MgO single crystals substrates by PLD method. We found that 120 nm thick STO films, deposited at 730 °C, present the smoothest surface and a minimum FWMH of the (002) reflection. High quality, smooth and free-crack YBa2Cu3O7-x (YBCO) thick superconducting films have then been fabricated using a deposition temperature of 800 °C on STO-buffered MgO substrates. A 373 nm thick YBCO/STO/MgO film can carry current densities Jc (77 K, 0 T) of 1.4 MA/cm2 and Jc (77 K, 5 T) of 0.14 MA/cm2. The Jc in high field overcomes the current transported in same experimental conditions by 180 nm thick YBCO film grown on Y2O3-decorated STO single crystal. For 1350 nm thick YBCO/STO/MgO film the Jc (77 K, 0 T) is about 0.8 MA/cm2 and Jc (77 K, 5 T) is 0.09 MA/cm 2.",
keywords = "Artificial pinning centers, Buffer layers, Critical current density, Thick films, YBaCuO",
author = "Paolo Mele and K. Matsumoto and T. Horide and A. Ichinose and M. Mukaida and Y. Yoshida and S. Horii",
year = "2007",
month = "6",
day = "1",
doi = "10.1109/TASC.2007.897422",
language = "English",
volume = "17",
pages = "3713--3716",
journal = "IEEE Transactions on Applied Superconductivity",
issn = "1051-8223",
publisher = "Institute of Electrical and Electronics Engineers Inc.",
number = "2",

}

TY - JOUR

T1 - Fabrication of thick YBa2Cu3O7-x films on optimized SrTiO3 buffered-MgO single crystals

AU - Mele, Paolo

AU - Matsumoto, K.

AU - Horide, T.

AU - Ichinose, A.

AU - Mukaida, M.

AU - Yoshida, Y.

AU - Horii, S.

PY - 2007/6/1

Y1 - 2007/6/1

N2 - In this work, we studied the optimum deposition conditions for SrTiO 3 (STO) buffers deposited on MgO single crystals substrates by PLD method. We found that 120 nm thick STO films, deposited at 730 °C, present the smoothest surface and a minimum FWMH of the (002) reflection. High quality, smooth and free-crack YBa2Cu3O7-x (YBCO) thick superconducting films have then been fabricated using a deposition temperature of 800 °C on STO-buffered MgO substrates. A 373 nm thick YBCO/STO/MgO film can carry current densities Jc (77 K, 0 T) of 1.4 MA/cm2 and Jc (77 K, 5 T) of 0.14 MA/cm2. The Jc in high field overcomes the current transported in same experimental conditions by 180 nm thick YBCO film grown on Y2O3-decorated STO single crystal. For 1350 nm thick YBCO/STO/MgO film the Jc (77 K, 0 T) is about 0.8 MA/cm2 and Jc (77 K, 5 T) is 0.09 MA/cm 2.

AB - In this work, we studied the optimum deposition conditions for SrTiO 3 (STO) buffers deposited on MgO single crystals substrates by PLD method. We found that 120 nm thick STO films, deposited at 730 °C, present the smoothest surface and a minimum FWMH of the (002) reflection. High quality, smooth and free-crack YBa2Cu3O7-x (YBCO) thick superconducting films have then been fabricated using a deposition temperature of 800 °C on STO-buffered MgO substrates. A 373 nm thick YBCO/STO/MgO film can carry current densities Jc (77 K, 0 T) of 1.4 MA/cm2 and Jc (77 K, 5 T) of 0.14 MA/cm2. The Jc in high field overcomes the current transported in same experimental conditions by 180 nm thick YBCO film grown on Y2O3-decorated STO single crystal. For 1350 nm thick YBCO/STO/MgO film the Jc (77 K, 0 T) is about 0.8 MA/cm2 and Jc (77 K, 5 T) is 0.09 MA/cm 2.

KW - Artificial pinning centers

KW - Buffer layers

KW - Critical current density

KW - Thick films

KW - YBaCuO

UR - http://www.scopus.com/inward/record.url?scp=34547442513&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=34547442513&partnerID=8YFLogxK

U2 - 10.1109/TASC.2007.897422

DO - 10.1109/TASC.2007.897422

M3 - Article

AN - SCOPUS:34547442513

VL - 17

SP - 3713

EP - 3716

JO - IEEE Transactions on Applied Superconductivity

JF - IEEE Transactions on Applied Superconductivity

SN - 1051-8223

IS - 2

ER -