Formation mechanism of Mg-Al layered double hydroxide-containing magnesium hydroxide films prepared on Ca-added flame-resistant magnesium alloy by steam coating

Kae Nakamura, Mika Tsunakawa, Yuta Shimada, Ai Serizawa, Takahiro Ishizaki

研究成果: Article査読

15 被引用数 (Scopus)

抄録

Corrosion resistant films were prepared on the Ca-added flame-resistant magnesium alloy AZCa612 by steam coating at different treatment time and temperature. The formation mechanism of the films was investigated by using the digital microscope, FE-SEM, XRD, FT-IR, XPS and the potentiodynamic polarization curve measurements in a 5 mass% NaCl aqueous solution. XRD, FT-IR and XPS studies indicated that the film was composed mainly of Mg(OH)2 and carbonated-based Mg–Al LDHs. In addition, MgCO3 and AlO(OH) were also incorporated slightly in the film. The formation mechanism of the film on AZCa612 was proposed that amorphous Mg(OH)2 was initially formed by reaction of steam and MgO as a natural oxide film on the substrate. With an increase in the temperature and pressure, the amorphous Mg(OH)2 was crystallized, and further increase in temperature, pressure, and treatment time induced the formation of Mg-Al LDH and AlO(OH) in the film.

本文言語English
ページ(範囲)436-443
ページ数8
ジャーナルSurface and Coatings Technology
328
DOI
出版ステータスPublished - 2017 11 15

ASJC Scopus subject areas

  • Chemistry(all)
  • Condensed Matter Physics
  • Surfaces and Interfaces
  • Surfaces, Coatings and Films
  • Materials Chemistry

フィンガープリント 「Formation mechanism of Mg-Al layered double hydroxide-containing magnesium hydroxide films prepared on Ca-added flame-resistant magnesium alloy by steam coating」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル