Formation of corrosion-resistant films on AlZnMg alloy by steam coating using acidic Zn(NO3)2 aqueous solutions+

Tetsuya Yokomizo, Yuta Shimada, Mika Tsunakawa, Ai Serizawa, Takahiro Ishizaki

研究成果: Article

抜粋

Corrosion-resistant films were fabricated on AlZnMg alloy by steam coating using an acidic aqueous solution of Zn(NO3)2 at different concentrations. X-ray diffraction patterns and Fourier transform-infrared spectrometer spectra demonstrated that nitrate-type ZnAl layered double hydroxide (LDH) and ZnO films were formed on the AlZnMg surface by steam coating at temperatures of 373, 433, and 473 K, using Zn(NO3)2 aqueous solution at 1000 mM. At 513 K, £-AlO(OH) films were formed on the AlZnMg surface by steam coating using 1 to 100 mM Zn(NO3)2 aqueous solution. The corrosion resistance of the films was investigated by potentiodynamic polarization curve measurements, which revealed that the £-AlO(OH) films prepared by steam coating at 513 K using 1 mM of Zn(NO3)2 aqueous solution was the most effective treatment for suppression of pitting corrosion and anodic current density.

元の言語English
ページ(範囲)1166-1172
ページ数7
ジャーナルMaterials Transactions
59
発行部数7
DOI
出版物ステータスPublished - 2018 1 1

ASJC Scopus subject areas

  • Materials Science(all)
  • Condensed Matter Physics
  • Mechanics of Materials
  • Mechanical Engineering

フィンガープリント Formation of corrosion-resistant films on AlZnMg alloy by steam coating using acidic Zn(NO<sub>3</sub>)<sub>2</sub> aqueous solutions<sup>+</sup>' の研究トピックを掘り下げます。これらはともに一意のフィンガープリントを構成します。

  • これを引用