Formation of texture during high temperature deformation of Ti-50·3 mol.% Al

Hiroshi Fukutomi, Koshiro Aoki, Shin ichi Takagi, Minoru Nobuki, Heinrich Mecking, Taichi Kamijo

研究成果: Article査読

8 被引用数 (Scopus)

抄録

Ti-50·3 mol.% Al was deformed in compression under various conditions. Texture as well as microstructure in the dynamically recrystallized state were investigated. One-to-one correspondence existed between the size of dynamically recrystallized grains and the peak stresses appearing in stress-strain curves. Formation of a fiber texture was confirmed. The texture developed with a decrease in peak stress. Extensive occurrence of strain-induced grain boundary migration was observed in the initial stage of dynamic recrystallization at the deformation conditions where sharp textures were formed after large deformation. Measurement of {021) pole figure suggested that the main component of the fibre texture was located between {011) and {021) (compression plane).

本文言語English
ページ(範囲)37-42
ページ数6
ジャーナルIntermetallics
2
1
DOI
出版ステータスPublished - 1994
外部発表はい

ASJC Scopus subject areas

  • 化学 (全般)
  • 材料力学
  • 機械工学
  • 金属および合金
  • 材料化学

フィンガープリント

「Formation of texture during high temperature deformation of Ti-50·3 mol.% Al」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル