The local grain orientations and the distribution of Y2Ba 4CuUOx (U-2411) phase are measured within melt-textured YBCO samples by means of electron backscatter diffraction (EBSD). In this work, several samples with varying addition (0.1-0.8 wt%) of depleted uranium oxide (DU) were analysed by means of EBSD. The embedded U-2411 particles were found to have sizes around 200 nm, some large particles being present in the samples with a high DU concentration. Combined EBSD and EDX analysis enabled the identification of the Kikuchi patterns of the U-2411 phase, so that a true three-phase EBSD scan (YBCO, Y2BaCuO5 and U-2411) becomes possible.