Improvement of thermal stability with alloy impregnation in Gd-Ba-Cu-O superconductors for pulsed field magnetization

Y. Kimura, H. Matsumoto, H. Fukai, N. Sakai, I. Hirabayashi, M. Izumi, M. Murakami

研究成果: Article査読

2 被引用数 (Scopus)

抄録

We present a post-fabrication treatment that improves thermal conductivity of bulk Gd-Ba-Cu-O magnets. A small hole about 1 mm in diameter was artificially drilled into the centre of bulk Gd-Ba-Cu-O 25 mm in diameter and 18 mm in thickness. An aluminium wire was inserted into the hole, and then the sample was subjected to the impregnation by using Bi- Su-Cd alloy. A pulsed-field magnetization was performed for Gd-Ba-Cu-O bulk with and without the alloy impregnation treatment. The temperature of samples was monitored with thermocouples and local magnetic field density was measured with a Hall sensor at several positions. The maximum temperature rise was depressed by 4 K and the trapped field was increased by 25 % at 44 K. The result shows that the alloy impregnation is very effective in enhancing the thermal conductivity and thereby improving the field trapping ability.

本文言語English
論文番号097
ページ(範囲)389-392
ページ数4
ジャーナルJournal of Physics: Conference Series
43
1
DOI
出版ステータスPublished - 2006 6 1

ASJC Scopus subject areas

  • 物理学および天文学(全般)

フィンガープリント

「Improvement of thermal stability with alloy impregnation in Gd-Ba-Cu-O superconductors for pulsed field magnetization」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル