Densification of exchange-spring magnet ribbons of NdxFe85-xCo8V1B6 (x = 7-11) alloys has been investigated. The starting ribbon powders containing amorphous parts were prepared by melt spinning and were compacted by using a Spark Plasma Sintering (SPS) method. SPS is a type of solid compression sintering similar to hot-pressing and the sintering promotion factor is self heat generation by electric discharges between particles when the on-off D.C. pulse is applied. The bulk magnets indicated the springback phenomenon, pointing to multiple phases of the Nd2Fe14B type and the α-Fe type, and had isotropic magnetic properties. With increasing Nd content, Br decreased from 1.05 T to 0.82 T and HcJ increased from 256 kA/m to 832 kA/m. These changes were equivalent to those of the starting ribbons following annealing. The grain sizes of these bulk magnets were about 40 nm when x = 7-11. Under optimum preparation conditions, bulk Nd10Fe75Co8V1B6 magnet indicated (BH)max = 134 kJ/m3 (16.8 MGOe).
|ジャーナル||IEEE Transactions on Magnetics|
|出版物ステータス||Published - 2001 7 1|
|イベント||8th Joint Magnetism and Magnetic Materials -International Magnetic Conference- (MMM-Intermag) - San Antonio, TX, United States|
継続期間: 2001 1 7 → 2001 1 11
ASJC Scopus subject areas
- Electronic, Optical and Magnetic Materials
- Electrical and Electronic Engineering