Melt-processed Gd-Ba-Cu-O superconductor with trapped field of 3 T at 77 K

S. Nariki, N. Sakai, M. Murakami

研究成果: Article査読

150 被引用数 (Scopus)

抄録

We fabricated a single-domain Gd-Ba-Cu-O bulk superconductor 65 mm in diameter and studied the microstructure, superconducting and field-trapping properties. Melt-processing was performed under a controlled oxygen partial pressure of 1.0% using a precursor containing Gd123 and Gd211 powders in a molar ratio of 2:1, with 0.5 wt% of Pt and 20 wt% of Ag2O added. The distribution of Ag and Gd211 particles was almost homogeneous. The addition of Ag was very effective in reducing the amount of cracking in the sample. The maximum trapped magnetic field recorded was 3.05 T at 77 K. We also measured the trapped field between two Gd-Ba-Cu-O bulk samples in order to minimize the demagnetizing effect and found that the trapped field reached 4.3 T at 77 K.

本文言語English
ページ(範囲)S126-S130
ジャーナルSuperconductor Science and Technology
18
2
DOI
出版ステータスPublished - 2005 2 1

ASJC Scopus subject areas

  • セラミックおよび複合材料
  • 凝縮系物理学
  • 金属および合金
  • 電子工学および電気工学
  • 材料化学

フィンガープリント

「Melt-processed Gd-Ba-Cu-O superconductor with trapped field of 3 T at 77 K」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル