Melt-processing of Ag-added LRE-Ba-Cu-O (LRE = Nd, Sm)

H. Ikuta, S. Ikeda, A. Mase, M. Yoshikawa, Y. Yanagi, Y. Itoh, T. Oka, U. Mizutani

研究成果: Article

35 引用 (Scopus)

抜粋

Large c-axis oriented single-grain samples of LRE-Ea-Cu-O with LRE = Nd and Sm have been prepared by the melt-process in a reduced oxygen atmosphere. We found that adding Ag to the starting materials worked very effectively in order to circumvent the problems which we encountered in the melt-process of large samples. With the c-axis aligning perpendicular to the sample surface, we successfully synthesized single-grained samples which are 18 and 33 mm in diameter for LRE = Nd and Sm, respectively. The strength of the trapped magnetic field at the center of a LRE = Sm sample was 0.96 T at 77 K. This value is approximately one-half larger than a melt-processed Y-Ba-Cu-O with a similar size.

元の言語English
ページ(範囲)109-117
ページ数9
ジャーナルApplied Superconductivity
6
発行部数2-5
DOI
出版物ステータスPublished - 1998 1 1
外部発表Yes

ASJC Scopus subject areas

  • Engineering(all)
  • Physics and Astronomy(all)

フィンガープリント Melt-processing of Ag-added LRE-Ba-Cu-O (LRE = Nd, Sm)' の研究トピックを掘り下げます。これらはともに一意のフィンガープリントを構成します。

  • これを引用

    Ikuta, H., Ikeda, S., Mase, A., Yoshikawa, M., Yanagi, Y., Itoh, Y., Oka, T., & Mizutani, U. (1998). Melt-processing of Ag-added LRE-Ba-Cu-O (LRE = Nd, Sm). Applied Superconductivity, 6(2-5), 109-117. https://doi.org/10.1016/S0964-1807(98)00091-X