Nanostructured epitaxial thin films of Fe-based superconductors with enhanced superconducting properties

Paolo Mele, K. Matsumoto, H. Nagayoshi, K. Fujita, Y. Yoshida, Y. Ichino, T. Kiss, A. Ichinose, M. Mukaida, B. Maiorov, F. F. Balakirev, S. A. Baily, L. Civale

研究成果: Conference article

1 引用 (Scopus)

抄録

Epitaxial Fe-Te-Se thin films were deposited by pulsed laser deposition at 250-600 °C on SrTiO3 (100, STO), MgO (100), LaAlO3 (100, LAO) and CaF2 (100) single crystal substrates. Best superconducting film was grown on CaF2: Tconset = 20.0 K and Tc0 = 16.18 K with Tdep = 300 °C, 45000 pulses, 3 Hz. The critical current density Jc at 4.2 K was 0.41 × 106A/cm2 at 0 T and 0.23×106 A/cm2 at 9 T. Angular dependence of Jc showed broad c-axis correlated peak when B ≥ 3 T.

元の言語English
ページ(範囲)35-44
ページ数10
ジャーナルMaterials Research Society Symposium Proceedings
1434
発行部数January
DOI
出版物ステータスPublished - 2012 1 1
外部発表Yes
イベント2012 MRS Spring Meeting - San Francisco, United States
継続期間: 2012 4 92012 4 13

Fingerprint

Superconducting films
Epitaxial films
superconducting films
Pulsed laser deposition
pulsed laser deposition
critical current
Single crystals
current density
Thin films
single crystals
Substrates
thin films
pulses
strontium titanium oxide
Iron-based Superconductors

ASJC Scopus subject areas

  • Materials Science(all)
  • Condensed Matter Physics
  • Mechanics of Materials
  • Mechanical Engineering

これを引用

Nanostructured epitaxial thin films of Fe-based superconductors with enhanced superconducting properties. / Mele, Paolo; Matsumoto, K.; Nagayoshi, H.; Fujita, K.; Yoshida, Y.; Ichino, Y.; Kiss, T.; Ichinose, A.; Mukaida, M.; Maiorov, B.; Balakirev, F. F.; Baily, S. A.; Civale, L.

:: Materials Research Society Symposium Proceedings, 巻 1434, 番号 January, 01.01.2012, p. 35-44.

研究成果: Conference article

Mele, P, Matsumoto, K, Nagayoshi, H, Fujita, K, Yoshida, Y, Ichino, Y, Kiss, T, Ichinose, A, Mukaida, M, Maiorov, B, Balakirev, FF, Baily, SA & Civale, L 2012, 'Nanostructured epitaxial thin films of Fe-based superconductors with enhanced superconducting properties', Materials Research Society Symposium Proceedings, 巻. 1434, 番号 January, pp. 35-44. https://doi.org/10.1557/opl.2012.1419
Mele, Paolo ; Matsumoto, K. ; Nagayoshi, H. ; Fujita, K. ; Yoshida, Y. ; Ichino, Y. ; Kiss, T. ; Ichinose, A. ; Mukaida, M. ; Maiorov, B. ; Balakirev, F. F. ; Baily, S. A. ; Civale, L. / Nanostructured epitaxial thin films of Fe-based superconductors with enhanced superconducting properties. :: Materials Research Society Symposium Proceedings. 2012 ; 巻 1434, 番号 January. pp. 35-44.
@article{a5621f463937451eb08a1da41653a108,
title = "Nanostructured epitaxial thin films of Fe-based superconductors with enhanced superconducting properties",
abstract = "Epitaxial Fe-Te-Se thin films were deposited by pulsed laser deposition at 250-600 °C on SrTiO3 (100, STO), MgO (100), LaAlO3 (100, LAO) and CaF2 (100) single crystal substrates. Best superconducting film was grown on CaF2: Tconset = 20.0 K and Tc0 = 16.18 K with Tdep = 300 °C, 45000 pulses, 3 Hz. The critical current density Jc at 4.2 K was 0.41 × 106A/cm2 at 0 T and 0.23×106 A/cm2 at 9 T. Angular dependence of Jc showed broad c-axis correlated peak when B ≥ 3 T.",
author = "Paolo Mele and K. Matsumoto and H. Nagayoshi and K. Fujita and Y. Yoshida and Y. Ichino and T. Kiss and A. Ichinose and M. Mukaida and B. Maiorov and Balakirev, {F. F.} and Baily, {S. A.} and L. Civale",
year = "2012",
month = "1",
day = "1",
doi = "10.1557/opl.2012.1419",
language = "English",
volume = "1434",
pages = "35--44",
journal = "Materials Research Society Symposium - Proceedings",
issn = "0272-9172",
publisher = "Materials Research Society",
number = "January",

}

TY - JOUR

T1 - Nanostructured epitaxial thin films of Fe-based superconductors with enhanced superconducting properties

AU - Mele, Paolo

AU - Matsumoto, K.

AU - Nagayoshi, H.

AU - Fujita, K.

AU - Yoshida, Y.

AU - Ichino, Y.

AU - Kiss, T.

AU - Ichinose, A.

AU - Mukaida, M.

AU - Maiorov, B.

AU - Balakirev, F. F.

AU - Baily, S. A.

AU - Civale, L.

PY - 2012/1/1

Y1 - 2012/1/1

N2 - Epitaxial Fe-Te-Se thin films were deposited by pulsed laser deposition at 250-600 °C on SrTiO3 (100, STO), MgO (100), LaAlO3 (100, LAO) and CaF2 (100) single crystal substrates. Best superconducting film was grown on CaF2: Tconset = 20.0 K and Tc0 = 16.18 K with Tdep = 300 °C, 45000 pulses, 3 Hz. The critical current density Jc at 4.2 K was 0.41 × 106A/cm2 at 0 T and 0.23×106 A/cm2 at 9 T. Angular dependence of Jc showed broad c-axis correlated peak when B ≥ 3 T.

AB - Epitaxial Fe-Te-Se thin films were deposited by pulsed laser deposition at 250-600 °C on SrTiO3 (100, STO), MgO (100), LaAlO3 (100, LAO) and CaF2 (100) single crystal substrates. Best superconducting film was grown on CaF2: Tconset = 20.0 K and Tc0 = 16.18 K with Tdep = 300 °C, 45000 pulses, 3 Hz. The critical current density Jc at 4.2 K was 0.41 × 106A/cm2 at 0 T and 0.23×106 A/cm2 at 9 T. Angular dependence of Jc showed broad c-axis correlated peak when B ≥ 3 T.

UR - http://www.scopus.com/inward/record.url?scp=84894758164&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=84894758164&partnerID=8YFLogxK

U2 - 10.1557/opl.2012.1419

DO - 10.1557/opl.2012.1419

M3 - Conference article

AN - SCOPUS:84894758164

VL - 1434

SP - 35

EP - 44

JO - Materials Research Society Symposium - Proceedings

JF - Materials Research Society Symposium - Proceedings

SN - 0272-9172

IS - January

ER -