Optimization of Mg Precursor Concentration to Obtain High Jc in MgB2 Synthesized with Ag Addition and Carbon Encapsulated Boron

Sai Srikanth Arvapalli, Muralidhar Miryala, Masato Murakami

研究成果: Article

1 引用 (Scopus)

抜粋

In this work, we report an optimum amount of Mg precursor required for obtaining high critical current density (Jc) of bulk MgB2 superconductor synthesized via solid state sintering. We add a slight excess of Mg precursor to balance its losses while formation of pinning phases and impurities such as Ag-Mg phases and MgO, respectively. Several amounts of Mg had been varied such as x = 1.05, 1.075, 1.1, 1.125, and 1.15 in MgxB2. To obtain the best critical current density values, we used carbon encapsulated boron (1.5% carbon) and added 4 wt% Ag. The X-ray diffraction analysis showed the presence of AgMg and AgMg3 phases and a minute amount of MgO. The SQUID measurements indicated that highest Jc of 350 kA/cm2 at 20 K and self-field in sample with x = 1.075. All results analyzed explain the improved critical current performance based on nanometer-sized Ag-Mg particles in the final product.

元の言語English
記事番号8000904
ジャーナルIEEE Transactions on Applied Superconductivity
29
発行部数5
DOI
出版物ステータスPublished - 2019 1 1

ASJC Scopus subject areas

  • Electronic, Optical and Magnetic Materials
  • Condensed Matter Physics
  • Electrical and Electronic Engineering

フィンガープリント Optimization of Mg Precursor Concentration to Obtain High J<sub>c</sub> in MgB<sub>2</sub> Synthesized with Ag Addition and Carbon Encapsulated Boron' の研究トピックを掘り下げます。これらはともに一意のフィンガープリントを構成します。

  • これを引用