Optimization of YbBa2Cu3Oy Thick Film Formation on MgO Substrates using Yb2BaO5 and liquid phase

A. Hattori, M. Muralidhar, A. Sai Srikanth, M. Murakami

研究成果: Conference article査読

抄録

The production of best thick YbBa2Cu3Oy (Yb123) films on MgO substrates are crucial for the utilization of this technology in silver sheeted wire as similar to Bi-2223. In this work, in order to optimize YbBa2Cu3Oy films on MgO substrates, a mixture of alpha-terpineol and 2-ethyl acetate was utilized as a solvent to which 100 nm sized stoichiometric powder mixture of Yb2BaO5, BaCuO2 and CuO was added and grinded for several hours to form a highly dense paste. Thick film precursors were prepared by spreading the paste over MgO substrates with a screen printing technique and various sintered and quench studies are done. Growth temperature is systematically varied between 800 and 950 °C for 30 minutes in air and quenched in liquid nitrogen. Similarly, sintering durations are varied systematically from 15 minutes to 8 hours. XRD reveals conformed that large Yb123 grains are formed when the thick films are sintered at 825 °C for 1 hour on MgO substrate. SEM micrographs are also in congruence with the XRD results depicting the giant Yb123 crystals. The present results clearly demonstrate that optimization of the growth temperature and time is crucial to obtain the large thick YbBa2Cu3Oy films on MgO substrates.

本文言語English
論文番号012011
ジャーナルJournal of Physics: Conference Series
1293
1
DOI
出版ステータスPublished - 2019 10 15
イベント31st International Symposium on Superconductivity, ISS 2018 - Tsukuba, Ibaraki, Japan
継続期間: 2018 12 122018 12 14

ASJC Scopus subject areas

  • Physics and Astronomy(all)

フィンガープリント 「Optimization of YbBa<sub>2</sub>Cu<sub>3</sub>O<sub>y</sub> Thick Film Formation on MgO Substrates using Yb<sub>2</sub>BaO<sub>5</sub> and liquid phase」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル