Patents relating to production of bulk ternary LRE-Ba 2Cu 3O y materials intended for applications at high magnetic fields and temperatures

Miryala Muralidhar, Milos Jirsa, Masaru Tomita

研究成果: Review article

7 引用 (Scopus)

抜粋

In this patent review the progress in technology and prospects of bulk ternary LRE-Ba 2Cu 3O y 'LRE-123' (LRE=light rare earth, Nd, Eu, Sm, Gd) superconductors are presented. Number of experiments has proven that ternary LRE-123 melt processed materials exhibit excellent properties appropriate for development of bulk high-field high-T c superconducting magnets. The key prerequisite for success in controlling flux pinning in these materials at high magnetic fields is creation of pinning defects with distinct superconducting properties compared to the superconducting matrix. In (Nd,Eu,Gd)-123 critical current density achieved the level of 10 5A/cm 2 at 65K in self-field and 5T and the irreversibility field B irr (the field limit above which the superconductor looses its ability to carry electric current) approached 15T at 77K. The high critical current density at low and intermediate fields, persisting up to the boiling point of liquid oxygen (90.2K), close to T c, is mainly due to size reduction of normal-conducting or insulating pinning defects up to nanoscale level. Such pinning sites are e.g. nanoscale secondary phase particles, Zr-, Nb-, Mo-, or Ti-oxides. In some particular (Nd,Eu,Gd)-123 compositions B irr increased twice due to a nanoscale planar substructure correlated with the regular twin structure.

元の言語English
ページ(範囲)4-17
ページ数14
ジャーナルRecent Patents on Materials Science
5
発行部数1
出版物ステータスPublished - 2012 1 1

ASJC Scopus subject areas

  • Materials Science(all)

フィンガープリント Patents relating to production of bulk ternary LRE-Ba <sub>2</sub>Cu <sub>3</sub>O <sub>y</sub> materials intended for applications at high magnetic fields and temperatures' の研究トピックを掘り下げます。これらはともに一意のフィンガープリントを構成します。

  • これを引用