DyBa2Cu3Oy (Dy-123) thick films were fabricated from Dy2BaO4, BaCuO2, and CuO powders. We have added 0, 1, 2, and 4 wt% of Ag2O. Mixture of alpha-terpineol and 2-ethyl acetate was used as a solvent, to which 100nm-sized stoichiometric powdered mixture was added and grinded for several hours to form a highly dense paste. Thick film precursors were prepared by spreading the paste on MgO substrates with a screen printing technique. The films were sintered with a double-step annealing process. The Dy-123 thick films obtained were of good quality. XRD analyses confirmed the formation of a high-quality c-axis oriented Dy-123 for films annealed at 1070oC for 10 min and at 880oC for 2 h. Scanning electron microscopy showed the formation of large flat grains. Onset Tc was 91 K according to magnetization measurements. The present results suggest that this process might be useful for the preparation of large-area superconducting thick films on MgO substrates in a short processing time.
|出版物ステータス||Published - 2015|
|イベント||27th International Symposium on Superconductivity, ISS 2014 - Tokyo, Japan|
継続期間: 2014 11 25 → 2014 11 27
|Other||27th International Symposium on Superconductivity, ISS 2014|
|期間||14/11/25 → 14/11/27|
ASJC Scopus subject areas
- Physics and Astronomy(all)