Preparation and characterization of rutile-TiO2 nanorods

Lei Miao, Sakae Tanemura, Shoichi Toh, Kenji Kaneko, Masaki Tanemura

研究成果: Article

8 引用 (Scopus)

抜粋

The controlled growth of densely assembled single-phase rutile-TiO2 nanorods was demonstrated by a heating-sol-gel template process with about -300 nm in diameter and several micrometers in length. Transmission electron microscopic observation reveals these rutile-TiO2 nanorods are the aggregates of many nanocrystallites growing preferentially to the [110] zone axis direction with about 10-30 nm in diameter. The calculation and comparison of d-spacing values with those of bulk values suggest the crystal structure of nanorods close to bulk materials. Selected area electron diffraction and energy dispersive X-ray spectroscopy measurements confirm that the obtained nanorods are rutile-TiO2 nanorods with good compositional uniformity and consist of distinct shape of nanocrystallites with 10-30 nm diameter.

元の言語English
ページ(範囲)59-62
ページ数4
ジャーナルJournal of Materials Science and Technology
20
発行部数SUPPL.
出版物ステータスPublished - 2004 12
外部発表Yes

ASJC Scopus subject areas

  • Ceramics and Composites
  • Mechanics of Materials
  • Mechanical Engineering
  • Polymers and Plastics
  • Metals and Alloys
  • Materials Chemistry

フィンガープリント Preparation and characterization of rutile-TiO<sub>2</sub> nanorods' の研究トピックを掘り下げます。これらはともに一意のフィンガープリントを構成します。

  • これを引用

    Miao, L., Tanemura, S., Toh, S., Kaneko, K., & Tanemura, M. (2004). Preparation and characterization of rutile-TiO2 nanorods. Journal of Materials Science and Technology, 20(SUPPL.), 59-62.