Preparation and properties of Bi2SiO5/Si structures

Masaki Yamaguchi, Kouji Hiraki, Takao Nagatomo, Yoichiro Masuda

研究成果: Article査読

14 被引用数 (Scopus)

抄録

Bismuth silicate (Bi2SiO5) films, expected as the intermediate buffer layer between the bismuth layer-structured ferroelectrics (BLSF) and silicon substrate were prepared on (100)-oriented silicon wafers by rf magnetron sputtering. The c-axis-oriented Bi2SiO5 films with smooth surface morphology were obtained at the substrate temperature of 400°C. The leakage current density is on the order of 10-10 A·cm-2, under the applied electric field of less than 350 kV·cm-1. From capacitance-voltage characteristics measurement results, it is worth noting that hysteresis is hardly observed. The interface trap density at the midgap is estimated to be approximately 6 × 1012 cm-2·eV-1. The numerical evaluation results indicate that the metal-ferroelectric-insulator-semiconductor (MFIS) capacitor can be reversed at a low applied voltage. This suggests that Bi4Ti3O12/Bi2SiO5/Si structures are suitable for application for ferroelectric memory devices.

本文言語English
ページ(範囲)5512-5516
ページ数5
ジャーナルJapanese Journal of Applied Physics, Part 1: Regular Papers and Short Notes and Review Papers
39
9 B
DOI
出版ステータスPublished - 2000 9

ASJC Scopus subject areas

  • Engineering(all)
  • Physics and Astronomy(all)

フィンガープリント 「Preparation and properties of Bi<sub>2</sub>SiO<sub>5</sub>/Si structures」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル