Preparation of thin porous titania films on stainless steel substrates for heat exchange (HEX) reactors

Mikihiro Nomura, Ben Meester, Joop Schoonman, Freek Kapteijn, Jacob A. Moulijn

研究成果: Article

14 引用 (Scopus)

抜粋

A porous titania film with pores of few micrometer sizes was prepared on a stainless steel support for a composite material of metal and inorganic oxide. The combination of a porous catalyst layer and a metal support improves the thermal conductivity compared with a traditional inorganic powder catalyst by an aid of a metal support. A porous titania film was obtained on a stainless steel support by the electrostatic sol-spray deposition (ESSD) method. Water in the parent sol was a key factor to obtain porous films. These porous films were cracked by a rapid temperature change during the cooling procedure after the deposition by the difference of the thermal expansion rate of stainless steel and titania. The parent sol was aged before a deposition to obtain a flexible structure to keep its structure. The obtained porous films comprised an aggregation of fibrous titania with few micrometer pores by SEM observation. This film was stable for a rapid temperature change. A porous titania film without any cracks were obtained on a stainless steel substrate using the ESSD method by an aging of the parent sol.

元の言語English
ページ(範囲)387-395
ページ数9
ジャーナルSeparation and Purification Technology
32
発行部数1-3
DOI
出版物ステータスPublished - 2003 7 1

ASJC Scopus subject areas

  • Analytical Chemistry
  • Filtration and Separation

フィンガープリント Preparation of thin porous titania films on stainless steel substrates for heat exchange (HEX) reactors' の研究トピックを掘り下げます。これらはともに一意のフィンガープリントを構成します。

  • これを引用