Pulsed field magnetization characteristics of a holed superconducting bulk magnet

K. Yokoyama, R. Igarashi, R. Togasaki, Tetsuo Oka

研究成果: Article

2 引用 (Scopus)

抄録

We have proposed a holed superconducting bulk magnet to trap the magnetic field efficiently in the high-performance material excited by pulsed field magnetization. Previously, a single pulsed field was applied with varying amplitudes of the magnetic fields and temperatures to a GdBCO bulk material with four 2-mm-diameter holes, and the time responses of flux density on the bulk surface and trapped field distributions were measured. The experimental results suggested that the number of holes was too high because a large distortion appeared in the trapped field distributions. In this paper, we processed only a single hole with a different hole size and investigated the magnetization characteristics. After estimating the trapped field performance by applying a single pulsed field with varying its amplitude and temperature in the original material, a 1-mm-diameter hole was drilled; then the hole was extended to 2 mm in diameter, and the same experiments were carried out in each sample. A total magnetic flux of both 1-mm-diameter hole and 2-mm-diameter hole samples was about 10 percent higher than that of a four-hole sample at a low temperature. On the other hand, the value of a 2-mm-diameter hole sample was the same as that of a four-hole sample at a high temperature. The experimental results suggested that about 1 mm in diameter was proper for the hole size.

元の言語English
ページ(範囲)117-121
ページ数5
ジャーナルPhysica C: Superconductivity and its Applications
518
DOI
出版物ステータスPublished - 2015 6 25
外部発表Yes

Fingerprint

Magnets
Magnetization
magnets
magnetization
Magnetic fields
Temperature
Magnetic flux
Fluxes
time response
Experiments
magnetic fields
magnetic flux
estimating
flux density
traps
temperature

ASJC Scopus subject areas

  • Electronic, Optical and Magnetic Materials
  • Condensed Matter Physics
  • Energy Engineering and Power Technology
  • Electrical and Electronic Engineering

これを引用

Pulsed field magnetization characteristics of a holed superconducting bulk magnet. / Yokoyama, K.; Igarashi, R.; Togasaki, R.; Oka, Tetsuo.

:: Physica C: Superconductivity and its Applications, 巻 518, 25.06.2015, p. 117-121.

研究成果: Article

@article{522654f69b2a46d4949c7c4bc4fd43ad,
title = "Pulsed field magnetization characteristics of a holed superconducting bulk magnet",
abstract = "We have proposed a holed superconducting bulk magnet to trap the magnetic field efficiently in the high-performance material excited by pulsed field magnetization. Previously, a single pulsed field was applied with varying amplitudes of the magnetic fields and temperatures to a GdBCO bulk material with four 2-mm-diameter holes, and the time responses of flux density on the bulk surface and trapped field distributions were measured. The experimental results suggested that the number of holes was too high because a large distortion appeared in the trapped field distributions. In this paper, we processed only a single hole with a different hole size and investigated the magnetization characteristics. After estimating the trapped field performance by applying a single pulsed field with varying its amplitude and temperature in the original material, a 1-mm-diameter hole was drilled; then the hole was extended to 2 mm in diameter, and the same experiments were carried out in each sample. A total magnetic flux of both 1-mm-diameter hole and 2-mm-diameter hole samples was about 10 percent higher than that of a four-hole sample at a low temperature. On the other hand, the value of a 2-mm-diameter hole sample was the same as that of a four-hole sample at a high temperature. The experimental results suggested that about 1 mm in diameter was proper for the hole size.",
keywords = "Flux jump, Pulsed field magnetization, Small hole, Superconducting bulk magnet, Total magnetic flux",
author = "K. Yokoyama and R. Igarashi and R. Togasaki and Tetsuo Oka",
year = "2015",
month = "6",
day = "25",
doi = "10.1016/j.physc.2015.06.008",
language = "English",
volume = "518",
pages = "117--121",
journal = "Physica C: Superconductivity and its Applications",
issn = "0921-4534",
publisher = "Elsevier",

}

TY - JOUR

T1 - Pulsed field magnetization characteristics of a holed superconducting bulk magnet

AU - Yokoyama, K.

AU - Igarashi, R.

AU - Togasaki, R.

AU - Oka, Tetsuo

PY - 2015/6/25

Y1 - 2015/6/25

N2 - We have proposed a holed superconducting bulk magnet to trap the magnetic field efficiently in the high-performance material excited by pulsed field magnetization. Previously, a single pulsed field was applied with varying amplitudes of the magnetic fields and temperatures to a GdBCO bulk material with four 2-mm-diameter holes, and the time responses of flux density on the bulk surface and trapped field distributions were measured. The experimental results suggested that the number of holes was too high because a large distortion appeared in the trapped field distributions. In this paper, we processed only a single hole with a different hole size and investigated the magnetization characteristics. After estimating the trapped field performance by applying a single pulsed field with varying its amplitude and temperature in the original material, a 1-mm-diameter hole was drilled; then the hole was extended to 2 mm in diameter, and the same experiments were carried out in each sample. A total magnetic flux of both 1-mm-diameter hole and 2-mm-diameter hole samples was about 10 percent higher than that of a four-hole sample at a low temperature. On the other hand, the value of a 2-mm-diameter hole sample was the same as that of a four-hole sample at a high temperature. The experimental results suggested that about 1 mm in diameter was proper for the hole size.

AB - We have proposed a holed superconducting bulk magnet to trap the magnetic field efficiently in the high-performance material excited by pulsed field magnetization. Previously, a single pulsed field was applied with varying amplitudes of the magnetic fields and temperatures to a GdBCO bulk material with four 2-mm-diameter holes, and the time responses of flux density on the bulk surface and trapped field distributions were measured. The experimental results suggested that the number of holes was too high because a large distortion appeared in the trapped field distributions. In this paper, we processed only a single hole with a different hole size and investigated the magnetization characteristics. After estimating the trapped field performance by applying a single pulsed field with varying its amplitude and temperature in the original material, a 1-mm-diameter hole was drilled; then the hole was extended to 2 mm in diameter, and the same experiments were carried out in each sample. A total magnetic flux of both 1-mm-diameter hole and 2-mm-diameter hole samples was about 10 percent higher than that of a four-hole sample at a low temperature. On the other hand, the value of a 2-mm-diameter hole sample was the same as that of a four-hole sample at a high temperature. The experimental results suggested that about 1 mm in diameter was proper for the hole size.

KW - Flux jump

KW - Pulsed field magnetization

KW - Small hole

KW - Superconducting bulk magnet

KW - Total magnetic flux

UR - http://www.scopus.com/inward/record.url?scp=84944514527&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=84944514527&partnerID=8YFLogxK

U2 - 10.1016/j.physc.2015.06.008

DO - 10.1016/j.physc.2015.06.008

M3 - Article

AN - SCOPUS:84944514527

VL - 518

SP - 117

EP - 121

JO - Physica C: Superconductivity and its Applications

JF - Physica C: Superconductivity and its Applications

SN - 0921-4534

ER -