Refinement of Nd-422 phase trapped in a Nd1+δBa2-δCu3O7-γ superconducting matrix

F. Frangi, S. I. Yoo, N. Sakai, M. Murakami

研究成果: Article

5 引用 (Scopus)

抜粋

The possibility of controlling Nd-422 phase dimension and morphology, both in the partially melted state and in the final superconducting matrix, was investigated. Nd-Ba-Cu-O samples were prepared by the melt powder melt growth (MPMG) technique. Precursor materials containing Nd as either Nd2O3 or Nd-422, formed during precursor quenching, were used. The role of Pt in Nd-422 refining was analyzed. The effect on Nd-422 nucleation and growth, of stoichiometries with increasing Nd-422 molar excesses (0%, 10%, 20%, and 40%) combined with different heating processes, up to the partially melted state, were examined. Uniformly distributed needle-like particles (1 μm diameter and 10-15 μm length) were obtained at 1120°C and resulted in a further refined distribution trapped in completely processed samples.

元の言語English
ページ(範囲)1990-2001
ページ数12
ジャーナルJournal of Materials Research
12
発行部数8
出版物ステータスPublished - 1997 8 1

ASJC Scopus subject areas

  • Materials Science(all)
  • Condensed Matter Physics
  • Mechanics of Materials
  • Mechanical Engineering

フィンガープリント Refinement of Nd-422 phase trapped in a Nd<sub>1+δ</sub>Ba<sub>2-δ</sub>Cu<sub>3</sub>O<sub>7-γ</sub> superconducting matrix' の研究トピックを掘り下げます。これらはともに一意のフィンガープリントを構成します。

  • これを引用