TY - JOUR
T1 - Resistance and inductance studies of Bi2−xPbxCa2Sr2Cu3Oy superconducting compounds
AU - Muralidhar, M.
AU - Rao, D. Mangapathi
AU - Somaiah, T.
AU - Babu, V. Hari
PY - 1990/5
Y1 - 1990/5
N2 - Bi2−xPbxCa2Sr2Cu3Oy compounds with (x = 0, 0.1, 0.2, 0.25, 0.3 and 0.4) were prepared by solid state reaction. The resistance and inductance results showed that transition temperature increases with increase in lead concentration. The highest value of Tc(0) observed is 109 K for Bi1.70Pb0.30Ca2Sr2 · Cu3Oy. The change of inductance per unit volume at liquid nitrogen temperature as a function of composition showed maximum change in x = 0.30 Pb‐doped sample. The results showed that the inductance change is maximum in samples which also showed highest Tc.
AB - Bi2−xPbxCa2Sr2Cu3Oy compounds with (x = 0, 0.1, 0.2, 0.25, 0.3 and 0.4) were prepared by solid state reaction. The resistance and inductance results showed that transition temperature increases with increase in lead concentration. The highest value of Tc(0) observed is 109 K for Bi1.70Pb0.30Ca2Sr2 · Cu3Oy. The change of inductance per unit volume at liquid nitrogen temperature as a function of composition showed maximum change in x = 0.30 Pb‐doped sample. The results showed that the inductance change is maximum in samples which also showed highest Tc.
UR - http://www.scopus.com/inward/record.url?scp=84985756760&partnerID=8YFLogxK
UR - http://www.scopus.com/inward/citedby.url?scp=84985756760&partnerID=8YFLogxK
U2 - 10.1002/crat.2170250520
DO - 10.1002/crat.2170250520
M3 - Article
AN - SCOPUS:84985756760
VL - 25
SP - 561
EP - 565
JO - Crystal Research and Technology
JF - Crystal Research and Technology
SN - 0232-1300
IS - 5
ER -