Self-regenerative field emission source

Masaki Tanemura, J. Tanaka, K. Itoh, T. Okita, L. Miao, S. Tanemura, S. P. Lau, L. Huang, Y. Agawa, M. Kitazawa

研究成果: Article査読

20 被引用数 (Scopus)

抄録

A self-regenerative field emission source was demonstrated. The emission source (cathode) consisted of carbon nanofibers (CNFs) grown on the tip of conical carbon protrusions on a graphite plate. CNFs were ∼25 nm in diameter, 0.3-2.5 μm in length and ∼1× 106 mm-2 in site density. Initial emission characteristics showed a threshold field of 3.05 Vμm with a current density of 1 μA cm2 and a field enhancement factor of 2860 from the Fowler-Nordheim plot assuming the work function of 4.6 eV for graphite. A lifetime test carried out for more than 40 h at a constant applied electric field of 10 Vμm in 10-4 Pa region disclosed a stable emission with a current density of 1.7-3.0× 10-4 A cm2 after a slight initial decrease in the emission current. Detailed morphological observations revealed that a thick layer of newly grown carbon fibers was formed on the cathode surface after the lifetime test which could be responsible for the observed stable and long-sustained emission under a nonultrahigh vacuum condition. Their growth was attributed to the surface diffusion of carbon atoms generated by sputtering of the carbon cathode with ionized residual gas molecules during the field emission process. Thus, the CNF-tipped carbon emitter was believed to be promising as a practical field electron emission source used under low vacuum.

本文言語English
論文番号193102
ページ(範囲)1-3
ページ数3
ジャーナルApplied Physics Letters
87
19
DOI
出版ステータスPublished - 2005 11月 7
外部発表はい

ASJC Scopus subject areas

  • 物理学および天文学(その他)

フィンガープリント

「Self-regenerative field emission source」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル